標準編號:	GB/T 16553-2017
中文名稱:	珠寶玉石 鑒定
英文名稱:	Gems-Testing
中標分類:	D59    其他非金屬礦
行業分類:	GB    國家標準
ICS分類:	39.060 39.060    珠寶 39.060
發布機構:	中華人民共和國國家質量監督檢驗檢疫總局 中國國家標準化管理委員會
發布日期:	2017-10-14
實施日期:	2018-5-1
標準狀態:	valid
替代舊標準:	GB/T 16553-2010 珠寶玉石 鑒定
翻譯語言:	英文
文件格式:	PDF
中文字符數:	93000 字
翻譯價格(元):	5580.0
交付時間:	付款后 1 個工作日

Codeofchina.com is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative. This standard is developed in accordance with the rules given in GB/T 1.1-2009. This standard replaces GB/T 16553-2010 Gems - Testing. The following main changes have been made with respect to 16553-2010 (the previous edition): ——The application scope is modified (see Clause 1). ——The references to terms and definitions in GB/T 16552 are added; the repeated terms and definitions of "phenomena", "heating", "diffusion", etc. are deleted; the terms and definitions of "color”, "colorless oiling” and "waxing” are deleted, those of "fluorescence" and "phosphorescence" are modified, and that of "inclusions" is added. (See Clause 3) ——The routine testing methods and special testing methods are combined as testing methods; wherein, the “UV fluorescence” is changed to “fluorescence observation”, and the “absorption spectrum” is incorporated into “UV-visible spectrum analysis”. (See 4.1) ——The principle and application scope of the testing methods such as infrared spectrum analysis and laser Raman spectrum analysis are modified; the operation steps in the testing methods such as infrared spectrum analysis, UV-visible spectrum analysis and laser Raman spectrum analysis are changed to the application in gems testing; luminescence spectrum analysis is added. (See 4.1) ——For the testing items, the “UV fluorescence” is changed to “fluorescence observation”, the absorption spectrum is deleted, and items such as infrared spectrum, UV-visible spectrum and Raman spectrum are added; the selection principle of the testing items is modified. (See 4.2) ——The infrared spectrum testing characteristics of each gem variety are added. (See Clause 5) ——The testing characteristics of varieties and subvarieties such as hauyne, sphalerite, balin stone, changhua stone, conch pearl and mammoth ivory are added, and those of turquoise are deleted. (See Clause 5) ——The enhancement and treatment types and testing characteristics of gems varieties such as diamond, emerald, spinel, turquoise, sugilite and amber are added and modified; the description of material properties as well as the testing characteristics of treatment methods such as dyeing, filling or impregnation and coating of gems varieties are regulated. (See Clause 5) ——The additions, deletions and medications are made accordingly in accordance with the modification of GB/T 16552 Gems - Nomenclature. This standard was proposed by the Ministry of Land Resources. This standard is under the jurisdiction of the National Technical Committee on Jewelry and Jade of Standardization Administration of China (SAC/TC 298). The previous editions of this standard are as follows: ——GB/T 16553-1996, GB/T 16553-2003 and GB/T 16553-2010. Gems - Testing 1 Scope This standard specifies the terms and definitions, testing methods, item selection and testing characters of gems. This standard is applicable to gems testing. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. GB/T 16552 Gems - Nomenclature 3 Terms and definitions For the purpose of this standard, the terms and definitions specified in GB/T 16552 as well as the followings apply. 3.1 crystal solid with a lattice structure, of which, the internal particles are regularly arranged in a regular periodic arrangement in space 3.2 crystalline crystalline solid (crystal) 3.3 crystalline aggregate block composed of numerous crystallines Note: crystalline aggregate includes phanerocrystalline aggregate and cryptocrystalline aggregate. 3.4 non-crystalline solid of non-lattice structure, of which, the internal particles are irregularly arranged in space 3.5 crystal system classification reflecting the symmetry of the crystal, which is divided into seven crystal systems according to the symmetry degree: equiaxial system, hexagonal system, tetragonal system, trigonal system, orthorhombic system, monoclinic system, and triclinic system 3.6 crystal habit habit of certain mineral of tending to crystallize into a certain form under certain external conditions 3.7 crystal twinning regular formation of two or more of the same crystals according to certain symmetry rule Note: it is classified into contact crystal twinning, interpenetrant crystal twinning and ring crystal twinning according to the individual formation mode of crystal twinning. The contact crystal twinning is further classified into simple contact crystal twinning and polysynthetic crystal twinning. 3.8 twinning striation linear striation appearing on the crystal face, cleavage plane or gems cutting plane of crystal twinning joint surface 3.9 crystal face plane encircling the crystal surface, which is naturally formed during crystal growth 3.10 striation straight striation formed by a series of so-called adjacent faces on a crystal face, also called growth striation or combination striation 3.11 color band uneven distribution of internal color in a band (or block) shape Note: the original color band is a change in color depth or color due to changes in medium composition and growth environment during crystal growth. 3.12 optic character phenomena generated due to the action of material in the incidence and propagation directions of light, including such characters as the isotropy and anisotropy of material, axiality and positive/negative characters of anisotropic material 3.13 isotropic material material with optic character the same in all directions Note: the equiaxial-system and non-crystalline materials are isotropic. 3.14 anisotropic material material with optic character different in each direction Note: all materials other than equiaxial-system and non-crystalline materials are anisotropic. 3.15 optic indicatrix optical indicator indicating the relationship between the vibration direction of light wave and the corresponding refractive index when the light wave propagates in a crystal 3.16 uniaxial crystal crystal with only one special direction (one optical axis), which is free of birefringence when the incident light is parallel to this direction Note: the crystals of trigonal system, tetragonal system, and hexagonal system are uniaxial. 3.17 biaxial crystal crystal with two special directions (two optical axes), which is free of birefringence when the incident light is parallel to the two directions Note: the crystals of orthorhombic system, monoclinic system and triclinic system are biaxial. 3.18 optic orientation the spatial relationship between the principal axis of the optic indicatrix and the crystallographic axis of the crystal Note: the uniaxial crystal gemstone is of positive character when its ordinary light refractive index (No) is less than the extraordinary light refractive index (Ne), otherwise, it is of negative character. The three main refractive indexes of the biaxial crystal gemstone are represented by Ng, Nm, and Np as large, medium and small, respectively; where Ng-Nm>Nm-Np, such gemstone is of positive character, otherwise, it is of negative character. 3.19 refractive index ratio of the propagation speed of light in air (or vacuum) to that in gem material Note: the refractive index in gems test is the relative refractive index measured in air. 3.20 birefringence the maximum difference between two or three main refractive indexes in anisotropic material, also called double refraction 3.21 pleochroism phenomenon that a anisotropic colorful gemstone presents different colors due to the selective absorption of light waves in different crystal directions, which is classified into dichroism and trichroism 3.22 dichroism phenomenon that a uniaxial crystal colorful gemstone presents two different colors in two main vibration directions 3.23 trichroism phenomenon that a biaxial crystal colorful gemstone presents three different colors in different main vibration directions 3.24 absorption spectrum spectrum generated by the gem material by selectively absorbing the light of continuous spectrum on it 3.25 luster light reflection capability and characteristics of the surface of gem material Note: it is classified into metallic luster, submetallic luster, adamantine luster and vitreous luster according to the luster intensity; special lusters caused by the aggregate or surface characteristics include greasy luster, waxy luster, pearly luster, silky luster, etc. 3.26 transparency degree of light transmission of gem material Note: it may be classified into transparent, semitransparent, translucent, semitranslucent and opaque. 3.27 fluorescence phenomenon that the gems emit visible light under the illumination of excitation light source Note: it is classified into strong, medium, weak and none according to the light intensity. UV light is generally used as excitation source in gems testing. 3.28 phosphorescence phenomenon that the gems continue to shine in a short time after removing the excitation light source Note: UV light is generally used as excitation source in gems testing. 3.29 play-of-color phenomenon that colors generated due to light interference or diffraction by certain special structures of gems change with the light source or observation direction

Foreword i 1 Scope 2 Normative references 3 Terms and definitions 4 Testing methods and item selection 4.1 Testing methods 4.2 Testing items and selection principle 5 Testing criteria 5.1 Natural gemstones 5.1.1 Diamond 5.1.2 Ruby 5.1.3 Sapphire 5.1.4 Chrysoberyl 5.1.5 Cat’s-eye 5.1.6 Alexandrite 5.1.7 Emerald 5.1.8 Aquamarine 5.1.9 Beryl 5.1.10 Tourmaline 5.1.11 Spinel 5.1.12 Zircon 5.1.13 Topaz 5.1.14 Peridot 5.1.15 Garnet 5.1.16 Rock Crystal 5.1.17 Fledspar 5.1.18 Scapolite 5.1.19 Kornerupine 5.1.20 Zoisite (tanzanite) 5.1.21 Epidote 5.1.22 Iolite 5.1.23 Sphene 5.1.24 Apatite 5.1.25 Pyroxene 5.1.26 Andalusite 5.1.27 Sillimanite 5.1.28 Kyanite 5.1.29 Apophyllite 5.1.30 Lazulite 5.1.31 Idocrase 5.1.32 Sinhalite 5.1.33 Taaffeite 5.1.34 Benitoite 5.1.35 Barite 5.1.36 Celestite 5.1.37 Calcite 5.1.38 Axinite 5.1.39 Cassiterite 5.1.40 Amblygonite 5.1.41 Dioptase 5.1.42 Euclase 5.1.43 Braziiianite 5.1.44 Danburite 5.1.45 Phenakite 5.1.46 Hauyne 5.1.47 Sphalerite 5.2 Natural gems 5.2.1 Feicui, Jadeite 5.2.2 Nephrite, Hetian Yu 5.2.3 Opal 5.2.4 Quartzite jade 5.2.5 Chalcedony (Agate/Jasper) 5.2.6 Silicified jade (Silicified Asbestos/Silicified Wood/Silicified Coral) 5.2.7 Serpentine 5.2.8 Dushan Yu 5.2.9 Charoite 5.2.10 Albite Jade 5.2.11 Rhodonite 5.2.12 Actinolite 5.2.13 Turquoise 5.2.14 Lapis Lazuli 5.2.15 Malachite 5.2.16 Chrysocolla 5.2.17 Prehnite. 5.2.18 Marble 5.2.19 Smithsonite. 5.2.20 Rhodochrosite 5.2.21 Dolomite 5.2.22 Fluorite. 5.2.23 Hydrogrossular 5.2.24 Talc 5.2.25 Datolite 5.2.26 Howlite 5.2.27 Sodalite 5.2.28 Hematite 5.2.29 Natural glass 5.2.30 Chicken-blood stone 5.2.31 Shoushan stone 5.2.32 Qingtian stone 5.2.33 Balin stone 5.2.34 Changhua stone 5.2.35 Brucite 5.2.36 Sugilite 5.2.37 Hemimorphite 5.2.38 Mica jade 5.2.39 Pectolite 5.2.40 Chlorite 5.3 Natural organic materials 5.3.1 Natural pearls 5.3.2 Cultured pearl (pearl) 5.3.3 Conch pearl 5.3.4 Coral 5.3.5 Amber 5.3.6 Jet 5.3.7 Ivory 5.3.8 Mammoth Ivory 5.3.9 Tortoise Shell 5.3.10 Shell 5.4 Manufactured products 5.4.1 Synthetic Diamond 5.4.2 Synthetic Ruby 5.4.3 Synthetic Sapphire 5.4.4 Synthetic Emerald 5.4.5 Synthetic Beryl 5.4.6 Synthetic Chrysoberyl 5.4.7 Synthetic Alexandrite 5.4.8 Synthetic Spinel 5.4.9 Synthetic Opal 5.4.10 Synthetic Quartz 5.4.11 Synthetic Rutile 5.4.12 Synthetic Cubic Zirconia 5.4.13 Synthetic Moissanite 5.4.14 Synthetic Jadeite 5.4.15 Yttrium Aluminium Garnet(YAG) 5.4.16 Gadolinium Gallium Garnet (GGG) 5.4.17 Strontium Titanate 5.4.18 Strontium Aluminate Borate 5.4.19 Plastic 5.4.20 Glass

珠寶玉石 鑒定 1范圍 本標準規定了珠寶玉石的術語和定義、鑒定方法和項目選擇及鑒定特征。 本標準適用于珠寶玉石鑒定。 2規范性引用文件 下列文件對于本文件的應用是必不可少的。凡是注日期的引用文件，僅注日期的版本適用于本文件。凡是不注日期的引用文件，其最新版本(包括所有的修改單)適用于本文件。 GB/T 16552珠寶玉石 名稱 3術語和定義 GB/T 16552界定的以及下列術語和定義適用于本文件。 3.1 晶體 crystal 具有格子構造的固體，其內部質點在空間作有規律的周期性重復排列。 3.2 晶質體crystalline 結晶質的固體(晶體)。 3.3 晶質集合體crystalline aggregate 由無數個結晶個體組成的塊體。 注：晶質集合體包括顯晶質集合體和隱晶質集合體。 3.4 非晶質體non-crystalline 組成物質的內部質點在空間上呈不規則排列，不具格子構造的固體物質。 3.5 晶系 crystal system 反映晶體對稱特點的晶體分類，按對稱程度分為七個晶系：等軸晶系、六方晶系、四方晶系、三方晶系、斜方晶系、單斜晶系、三斜晶系。 3.6 晶體習性crystal habit 某種礦物在一定的外界條件下，趨向于結晶成某一種形態的特性。 3.7 雙晶crystal twinning 兩個或兩個以上的同種晶體按一定的對稱規律形成的規則連生。 注：按雙晶個體連生方式分為接觸雙晶、穿插雙晶和環狀雙晶。接觸雙晶又分為簡單接觸雙晶和聚片雙晶。 3.8 雙晶紋twinning striation 雙晶接合面在晶面、解理面或寶石切磨平面上呈現的線狀條紋。 3.9 晶面crystal face 晶體生長過程中自然形成的，包圍晶體表面的平面。 3.10 晶面條紋 striation 晶面上由一系列所謂的鄰接面構成的直線狀條紋，也稱生長條紋或聚形條紋。 3.11 色帶 color band 晶體內部顏色呈帶狀(或塊狀)不均勻分布的現象。 注：原生色帶是晶體生長過程中，由于介質成分及生長環境變化，導致顏色深淺變化或色彩的變化。 3.12 光性特征optic character 材料對入射光的方向和傳播方向發生作用，而產生的各種現象，包括材料的均質性、非均質性、非均質體的軸性和正負光性等特征。 3.13 光性均質體isotropic material 光學性質在各個方向上均相同的物質，簡稱均質體。 注：等軸晶系和非晶質的材料為光性均質體。 3.14 光性非均質體anisotropic material 光學性質在各個方向不同的物質，簡稱非均質體。 注：除等軸晶系和非晶質的材料外，均為光性非均質體。 3.15 光率體optic indicatrix 表示光波在晶體中傳播時，光波振動方向與相應折射率之間關系的一種光性指示體。 3.16 一軸晶 uniaxial crystal 只有一個特殊方向(一個光軸)，當光平行該方向入射時不發生雙折射的晶體。 注：三方晶系、四方晶系、六方晶系的晶體為一軸晶。 3.17 二軸晶biaxial crystal 具有兩個特殊方向(二個光軸)，當光平行該二個方向入射時不發生雙折射的晶體。 注：斜方晶系、單斜晶系、三斜晶系的晶體為二軸晶。 3.18 光性方位optic orientation 光率體主軸與晶體結晶軸之間的空間關系。 注：一軸晶寶石當其常光折射率(No)小于非常光折射率(Ne)時，為正光性(positive character)。反之，為負光性(negative character)；二軸晶寶石三個主折射率值按大、中、小分別用Ng、Nm、Np表示，當Ng-Nm>Nm-Np時，為正光性，反之為負光性。 3.19 折射率 refractive index 光在空氣(或真空)中與在珠寶玉石材料中傳播速度的比值，也稱折光率。 注：珠寶玉石檢測中的折射率是在空氣中測得的相對折射率。 3.20 雙折射率 birefringence 非均質體中兩個或三個主折射率之間的最大差值，也稱重折射率(或重折光率)。 3.21 多色性pleochroism 非均質的彩色寶石，由于不同結晶方向上對光波的選擇性吸收，呈現不同顏色的現象，分為二色性和三色性。 3.22 二色性dichroism 一軸晶彩色寶石，在二個主振動方向上，呈現二種不同顏色的現象。 3.23 三色性trichroism 二軸晶彩色寶石，在不同主振動方向上，呈現三種不同顏色的現象。 3.24 吸收光譜absorption spectrum 連續光譜的光照射珠寶玉石材料時，被選擇吸收而產生的光譜。 3.25 光澤luster 珠寶玉石材料表面反射光的能力和特征。 注：按光澤的強弱分為：金屬光澤(metallic luster)、半金屬光澤(submetallic luster)、金剛光澤(adamantine luster)和玻璃光澤(vitreous luster)；由集合體或表面特征所引起的特殊光澤有：油脂光澤(greasy luster)、蠟狀光澤(waxy luster)、珍珠光澤(pearly luster)、絲絹光澤(silky luster)等。 3.26 透明度transparency 珠寶玉石材料透光的程度。 注：可分為透明(transparent)、亞透明(semitransparent)、半透明(translucent)、微透明(semitranslucent)和不透明(opaque)。 3.27 熒光fluorescence 珠寶玉石在激發光源照射下，發出可見光的現象。 注：按發光的強弱分為強、中、弱、無。珠寶玉石鑒定中的激發源常用紫外光。 3.28 磷光 phosphorescence 激發光源撤除后，珠寶玉石在短時間內繼續發光的現象。 注：珠寶玉石鑒定中的激發源常用紫外光。 3.29 變彩效應play-of-color 珠寶玉石的某些特殊結構，對光的干涉或衍射作用而產生的顏色，隨光源或觀察方向的變化而變化的現象。 3.30 暈彩效應 iridescence 因某些特殊結構對光的干涉、衍射等作用，在珠寶玉石內部或表面產生光譜色的現象。 3.31 砂金效應 aventurescence 寶石內部細小片狀礦物包體對光的反射所產生的閃爍現象。 3.32 色散dispersion 當白色復合光通過具棱鏡性質的珠寶玉石材料時，分解成不同波長光譜的現象。 3.33 色散值dispersion value 反映材料色散強度的物理量。 注：理論上用該材料相對于紅光(B＝686.7 nm)的折射率與紫光(G=450.8 nm)的折射率的差值來表示，差值越大，色散強度越大。 3.34 密度density 單位體積物質的質量，單位是g/cm3。 3.35 硬度hardness 材料抵抗外來刻劃、壓入或研磨等機械作用的能力。 注：珠寶玉石硬度采用礦物學中的摩氏硬度(Mobs’hardness)表示。 3.36 解理cleavage 晶體在外力作用下沿一定的結晶方向裂開呈光滑平面的性質。 注：解理分為極完全、完全、中等、不完全、無。 3.37 斷口 fracture 晶體在外力作用下產生不規則破裂面的性質。 注：常見斷口類型有不平坦狀、鋸齒狀、貝殼狀等。 3.38 裂理parting 晶體在外力作用下沿一定結晶方向(如雙晶結合面)產生破裂的性質。 3.39 內部特征 internal characteristics 寶石材料中所含的固相、液相、氣相包裹體，特殊類型的包裹體(如負晶)及與寶石的晶體結構有關的現象。 注：如生長紋、色帶、雙晶紋、解理、裂理等。 3.40 外部特征 external characteristics 除晶形、顏色、透明度和光澤外，與寶石晶體結構有關的特殊現象，以及寶石在切磨拋光過程中留下的現象。 注1：常見的晶體外部特征有晶面橫紋、縱紋、雙晶紋、生長凹坑、生長丘及蝕象、溶丘等現象。 注2：常見的切磨寶石外部特征有刮痕、拋光紋(痕)、微缺口、空洞、損傷、燒痕、撞擊痕、須狀腰棱、額外刻面、棱線尖銳或圓滑等現象。 3.41 包裹體 inclusions 影響珠寶玉石整體均一性的，與主體有成分、相態、結構或顏色等差異的內、外部特征，可簡稱為包體。 注：如礦物包體、氣液包體、雙晶紋、斷口、解理、色帶等。 4鑒定方法和項目選擇 4.1鑒定方法 4.1.1 肉眼觀察 4.1.1.1方法原理：球寶玉石的某些性質，可以通過肉眼觀察的方法來確定，包括顏色、形狀、透明度、光澤、特殊光學效應、解理、斷口以及某些內外部特征。 4.1.1.2適用范圍：各種類型的珠寶玉石。 4.1.1.3操作步驟： a)借助自然光線或人工光源照明，首先觀察顏色、形狀、透明度、光澤、特殊光學效應等項目。 b)觀察是否具解理、斷口及某些切工特征。 c)若是晶體原石，可根據晶體形態，判斷所屬晶族或晶系。 d)在光源照明下，觀察較為明顯的內部特征。 4.1.1.4結果表示： a)根據肉眼觀察直接描述。 b)描述顏色時，直接用組成白光的光譜色或其混合色及白色、黑色、無色來描述。常以主色在后，輔色在前，如：黃綠色、綠黃色。必要時在顏色前加上深淺及明暗程度的描述，如：淺黃綠色，暗綠色。 c)描述形狀時，具晶形的原石可描述其晶形組成單形或聚形，并可據此判斷所屬晶系、晶族。已加工的珠寶玉石可根據加工形狀直接描述。如：橢圓形刻面、橢圓形弧面、圓球狀等。 4.1.2放大檢查 4.1.2.1方法原理：利用光學組件將珠寶玉石的微小內、外部特征進行放大，以便于觀察。 4.1.2.2儀器：各種類型的放大鏡和顯微鏡。 4.1.2.3適用范圍：各種類型的珠寶玉石。 4.1.2.4操作步驟： a)將樣品擦洗干凈，置于放大鏡或顯微鏡下。 b)用反射光觀察樣品的外部特征，用透射光或強光照明觀察樣品的內部特征。 c)特殊情況下，可附加散射白板、油浸等方法，觀察內部生長紋、顏色分布等特征。 d)從各個角度觀察，并記錄觀察現象，作為判斷依據。 4.1.2.5結果表示：直接描述所觀察到的內、外部特征，特別是具鑒定意義的特征。 4.1.3折射率 雙折射率 4.1.3.1方法原理：不同珠寶玉石材料具有特征的折射率或折射率范圍。通過測定折射率和雙折射率，可判斷珠寶玉石的光性特征，如非均質體/均質體、一軸晶/二軸晶甚至光性符號。 4.1.3.2儀器：阿貝型寶石折射儀，反射型折射儀。要求如下： a)阿貝型寶石折射儀，最小分度值為0.01； b)接觸油的折射率N油常為1.79～1.81； c)測量范圍：1.35～N油，測量上限值取決于接觸油的折射率N油。 4.1.3.3適用范圍：適用于具光滑面的珠寶玉石。下列情況下不易或不能測定折射率、雙折射率： a)樣品無光滑面(如拋光面、晶面等)，不易測定折射率、雙折射率。 b)樣品過小(平面直徑<2 mm)或樣品所鑲嵌的金屬超出樣品平面時，不易測定折射率、雙折射率。 c)樣品與折射儀接觸面過小(如小刻面、弧面)時，可用點測法測定折射率，但不易測定雙折射率。 d)樣品折射率超過折射儀及接觸油的測量范圍時，不能測定折射率、雙折射率。 e)接觸油對樣品有損害時(如多孔隙或結構松散的樣品)，不能測定折射率、雙折射率。 f)樣品為晶質集合體或有機寶石時，不易測定雙折射率。 4.1.3.4操作步驟： a)清洗或擦拭被測樣品。 b)將適量的接觸油滴在測量臺上。 c)將樣品的拋光面或晶面朝下，輕放于測量臺的接觸油上。 d)全方位轉動樣品和偏光片，并由觀測目鏡讀出明暗交界線的刻度值即折射率值。 e)非均質體可測得一個最大值和一個最小值，兩值之差即為雙折射率。 f)依據明暗交界線的變化情況，可判斷樣品的光性特征。 4.1.3.5結果表示： a)具光滑平面珠寶玉石折射率、雙折射率的實測值，保留到小數點后三位。 b)接觸面小的珠寶玉石如弧面型、小刻面珠寶玉石、原石等，用點測法測得折射率，可保留到小數點后兩位，并在其后加注“(點測法)”。點測法的分辨力通常為±0.01。 c)遇4.1.3.3中不易或不能測定折射率、雙折射率情況時，可標注“不可測”。 d)樣品折射率超過折射儀及接觸油測量范圍時，可用“>N油”表示。當N油為1.79或1.81時.可表示為>1.79或>1.81。 4.1.4光性特征 4.1.4.1方法原理：根據光的傳播方式及特征，珠寶玉石材料可分為均質體和非均質體；非均質體進一步分為一軸晶和二軸晶；根據光軸特點，一軸晶和二軸晶可各自分為正光性和負光性。通過判斷光性特征，可以輔助鑒定珠寶玉石種屬。 4.1.4.2儀器：偏光鏡，偏光顯微鏡，折射儀，二色鏡。 4.1.4.3適用范圍： a)偏光鏡檢測光性特征時，適用于透明一半透明的珠寶玉石材料。應注意； 1)寶石內部含大量包體或裂隙時，測試的可靠性差。 2)某些光性均質體，由于內部應力作用或其他作用，會呈現異常消光。 3)折射率很高的材料，由于外界光線經寶石反射后的反射光會產生偏振化，影響判斷結果。 b)偏光顯微鏡適用于粒度小或薄片狀寶石。 c)折射儀適用于折射率在折射儀測量范圍內、具光滑平面的珠寶玉石材料。詳見4.1.3折射率、雙折射率。 d)二色鏡適用于彩色非均質(即具多色性)的透明至半透明珠寶玉石材料。詳見4.1.5多色性。 4.1.4.4操作步驟(偏光鏡)：折射儀和二色鏡的操作步驟詳見4.1.3和4.1.5。偏光鏡的操作步驟如下： a)使儀器上下偏振片處于正交位置(全黑)。 b)把樣品置于載物臺上。 c)轉動樣品或載物臺，觀察樣品的明暗變化，確定樣品為均質體或非均質體(在油浸槽中觀察效果更佳)。 d)如需測定樣品的軸性和光性，先找出光軸所在方位，即干涉色最高方位，使其光軸直立然后將干涉球置于樣品之上，根據干涉圖形態確定軸性(即一軸晶、二軸晶)，再用消色板判斷樣品的光性(正光性、負光性)。 4.1.4.5結果表示： a)根據觀測結果表示為均質體、非均質體、均質集合體、非均質集合體。 b)對非均質體寶石，必要時可在非均質體后用括號表示出一軸晶或二軸晶，甚至其光性符號。如非均質體(一軸晶，十)或(二軸晶，一)等。 4.1.5 多色性 4.1.5.1方法原理：當光進入非均質體寶石時，分解成兩束振動方向相互垂直的偏振光，該兩束光的傳播速度有所不同，寶石對該兩束光產生的選擇性吸收也有差異，使不同方向上呈現的顏色色調或深淺有所不同，即多色性。一軸晶可見二色性，二軸晶寶石可見二色性或三色性。多色性的明顯程度，分為強、中、弱、無。根據多色性可以輔助判斷彩色寶石的光性特征及寶石晶體結構的定向。 4.1.5.2儀器：二色鏡。 4.1.5.3適用范圍：多色性觀察適用于彩色透明至半透明非均質體寶石。下列情況不易或不能觀察多色性： a)不透明或透明程度差的寶石，無法或不易觀測多色性； b)均質體及無色的非均質體寶石，無多色性； c)淺色非均質體寶石的多色性常不明顯； d)晶質集合體的珠寶玉石，不能觀測多色性。 4.1.5.4操作步驟： a)使用自然光或白熾燈光透射觀察。 b)將樣品置于二色鏡前適當位置。 c)轉動樣品或二色鏡，在不同方向上觀察。 d)觀察二色鏡兩個窗口中的顏色變化，可以是顏色深淺或色調的變化。 4.1.5.5結果表示： a)直接描述觀測到變化明顯的兩種或三種顏色，顏色間用逗號分開。如：藍寶石的二色性：藍，綠藍。 b)不透明或透明程度差的樣品，無法或不易觀測多色性時，表示為“不可測”。 c)均質體及無色非均質體寶石，無多色性，表示為“無”。 d)非均質集合體珠寶玉石，多色性不易觀測，表示為“不可測”。 4.1.6熒光觀察 4.1.6.1方法原理：某些珠寶玉石受到紫外光輻照時，會發出可見光。根據熒光強度及有無熒光反應可分為強、中、弱、無。根據樣品在長、短波紫外光下的熒光顏色和熒光強度可輔助判斷珠寶玉石種屬、天然與合成及是否經處理等。某些具磷光的珠寶玉石在停止紫外光照射后，仍能在一定時間繼續發出可見光。 4.1.6.2儀器：紫外燈(具365 nm長波紫外光和254 nm短波紫外光)。 4.1.6.3適用范圍：適用于任何樣品短時間的熒光觀察。 4.1.6.4操作步驟： a)在未打開紫外燈開關之前，將樣品放在樣品臺上。 b)分別按長波和短波按鈕，觀察樣品的熒光反應。 c)如需觀察樣品磷光，關閉開關，繼續觀察。 4.1.6.5結果表示：熒光觀察為描述項目，可分別描述樣品在長波和短波紫外光下的熒光強度和熒光顏色。描述時熒光強度在前，熒光顏色在后，中間用逗號分開，如長波：強，藍白；短波：中，藍白。 4.1.7質量 4.1.7.1方法原理：利用天平等衡器對珠寶玉石的質量進行稱量。 4.1.7.2儀器：天平，電子天平，電子秤等衡器。要求如下： a)當樣品質量m≤1 g時，分度值不大于0.001 g； b)當樣品質量在1 g