Codeofchina.com is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative.
This standard is developed in accordance with the rules given in GB/T 1.1-2009.
This standard replaces GB/T 246-2007 Metallic materials-Tube-Flattening test in whole. The following technical changes have been made with respect to GB/T 246-2007:
--The title is modified as "Metallic materials-Tube-Flattening test";
--"Scope" is modified (see chapter 1);
--Headings are added for Table 1 and Figure 1 respectively Table title and figure caption is added in Table 1 and Figure 1 respectively; the note of pipe wall thickness symbol in table 1 is modified (see Table 1 and Figure 1);
--"Test principle" is modified (see Chapter 3);
--Editorial changes are modified for "test procedure" (see Chapter 6);
--"Daylight opening" of Chapter 7 d) in original standard is modified as "the distance (H) between two platens under the force".
This standard is identical with ISO 8492:2013 Metallic materials-Tube-Flattening Test.
The following editorial changes have been made in this standard:
--Table title and figure caption is added in Table 1 and Figure 1 respectively.
This standard was proposed by China Iron and Steel Industry Association.
This standard is under jurisdiction of SAC/TC 183 National Technical Committee on Iron and Steel of Standardization Administration of China.
The previous editions of the standard replaced by this standard are as follows:
-GB 246-1963, GB 246-1982, GB/T 246-1997, GB/T 246-2007.
?
Metallic Materials-Tube-Flattening Test
1 Scope
This standard specifies methods of flattening test for the determination of plastic deformation of metallic conduit with circular cross-section, which can be used to reveal the defects.
In addition to the relevant product standards, this standard is applicable to metallic conduits with outer diameter no more than 600mm and wall thickness no more than 15% of the outer diameter.
2 Symbols, terms and units
See Table 1 and Figure 1 for the symbols, terms and units adopted in this standard.
Table 1 Symbols, Terms and Units
Symbol Term Unit
aa Wall thickness mm
b Inner width of sample after flattening mm
D Outer diameter of metallic conduit mm
H Distance between two platens under the force mm
L Sample length mm
a This parameter is also represented by other symbols in the steel pipe standard.
3 Principle
Flatten the sample of metal pipe end or sample with specified length, cut from a tube in a direction perpendicular to the longitudinal axis [See Figure 1 a) and Figure 1 b) ] , until the value of distance between platens under the action of flattening force meet the requirements of the relevant product standards.
If it's closed flattening, the width of inner surface contact area shall be at least half of the inner width b after normal flattening [see Figure 1 c)].
(b) (c)
Figure 1 Schematic Diagram for the Flattening Test
4 Apparatuses
The test machine shall be able to flatten the sample to the specified distance H between the two parallel platens which shall be of sufficient rigidity.
The width of the platen shall be greater than that of the flattened sample, i.e., at least 1.6D. And the length of the platen shall be not less than the sample length.
Foreword i
Introduction ii
1 Scope
2 Symbols, terms and units
3 Principle
4 Apparatuses
5 Sample
6 Procedures
7 Report
ICS 77.040.10
H 23
GB
中華人民共和國國家標準
GB/T 246—2017/ISO 8492:2013
代替GB/T 246—2007
金屬材料 管 壓扁試驗方法
Metallic materials—Tube—Flattening test
(ISO 8492:2013, IDT)
2017-07-12發布 2018-04-01實施
中華人民共和國國家質量監督檢驗檢疫總局 發布
中國國家標準化管理委員會
?
前 言
本標準按照GB/T 1.1—2009給出的規則起草。
本標準代替GB/T 246—2007《金屬 管 壓扁試驗方法》，與GB/T 246—2007相比主要技術變化如下：
——標準名稱更改為《金屬材料 管 壓扁試驗方法》；
——修改了“范圍”的表述(見第1章）；
——表1和圖1分別增加了表題和圖題;修改了表1中管壁厚度符號的注(見表1、圖1);
——修改了“試驗原理”的表述（見第3章）；
——對“試驗程序”進行了編輯性修改（見第6章）；
——將原標準第7章d)“壓板間距”改為“力作用下兩壓板之間的距離（H）”。
本標準使用翻譯法等同采用ISO 8492:2013《金屬材料 管 壓扁試驗方法》。
本標準做了下列編輯性修改：
——表1和圖1分別增加了表題和圖題。
本標準由中國鋼鐵工業協會提出。
本標準由全國鋼標準化技術委員會(SAC/TC 183)歸口。
本標準起草單位：中華人民共和國常熟出入境檢驗檢疫局、浙江金洲管道科技股份有限公司、國家鋼鐵及制品質量監督檢驗中心、冶金工業信息標準研究院。
本標準主要起草人：王衛忠、盧書媛、楊偉芳、劉彥、董莉、俞璐、徐海斌、黃飛。
本標準所代替標準的歷次版本發布情況為：
—-GB 246—1963、GB 246—1982、GB/T 246—1997、GB/T 246—2007。
?
金屬材料 管 壓扁試驗方法
1范圍
本標準規定了測定圓形橫截面金屬管塑性變形能力的壓扁試驗方法，也可用來揭示其缺陷。
除相關產品標準規定以外，本標準適用于外徑不超過600 mm且壁厚不超過外徑15%的金屬管。
2符號、名稱和單位
本標準使用的符號、名稱和單位見表1和圖1。
表1符號、名稱和單位
符 號 名 稱 單 位
aa 管壁厚度 mm
b 壓扁后試樣的內寬度 mm
D 金屬管外徑 mm
H 力作用下兩壓板之間的距離 mm
L 試樣長度 mm
a在鋼管標準中也用其他符號表示此參數。
3試驗原理
對從垂直于金屬管縱軸線方向截取的規定長度的金屬管試樣或金屬管端部試樣施加力進行壓扁 [見圖1a)和圖1b)]，直至在力的作用下兩壓板之間的距離達到相關產品標準所規定的值。
如為閉合壓扁，試樣內表面接觸區域的寬度應至少為正常壓扁后試樣內寬度b的一半[見圖1c)]。
(a) (b) (c)
圖 1 壓扁試驗示意圖
4 試驗設備
試驗機應能將試樣壓扁至規定的兩平行壓板之間的距離H。壓板應具有足夠剛度。
?
壓板的寬度應超過壓扁后的試樣寬度，即至少為1.6D。壓板的長度應不小于試樣的長度。
5試樣
5.1 試樣長度L應不小于10 mm,但不超過100mm。試樣的棱邊允許用銼或其他方法將其倒圓或倒角。
注：如果試驗結果滿足試驗要求，可以不對試樣的棱邊倒圓或倒角。
5.2 當在一根全長度管的管端進行試驗時，應在距管端面為試樣長度處垂直于管縱軸線切割，且切割深度應至少達外徑的80%。
6試驗程序
6.1試驗一般應在10℃~35℃的室溫范圍內進行。對溫度要求嚴格的試驗，試驗溫度應為23℃±5℃。
6.2試樣置于兩壓板之間。
6.3焊接管的焊縫應置于相關產品標準所規定的位罝。
6.4沿垂直于管縱軸線方向移動壓板進行壓扁。
6.5若有爭議，壓板的移動速率不應超過25mm/min。
6.6對壓扁試驗結果的評定應根據相關產品標準的要求。當產品標準中沒做規定時，在不使用放大鏡的情況下，如果無可見裂紋,應評定為合格。僅在試樣棱角處的輕微開裂不應作為判廢依據。
7試驗報告
如適用，應根據相關產品標準的要求提供試驗報告。試驗報告至少應包含下列內容：
a)本標準編號;
b)試樣標識;
c)試樣尺寸;
d)力作用下兩壓板之間的距離（H）;
e)如為焊接管，焊縫的位置；
f)試驗結果。