標準編號:	Q/BQB 403-2003
中文名稱:	冷連軋低碳鋼板及鋼帶
英文名稱:	Cold-rolled low carbon steel plate and steel strip
行業分類:	Q/    企業標準
發布日期:	2003-6-4
實施日期:	2003-12-15
標準狀態:	valid
翻譯語言:	英文
文件格式:	PDF
中文字符數:	7000 字
翻譯價格(元):	290.0
交付時間:	付款后 1 個工作日

Codeofchina.com is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative. Tandem Cold Rolling Low-carbon Steel Sheet and Strip 1 Scope This standard specifies such requirements of tandem cold rolling low-carbon steel sheet and strip as classification and code, dimension, appearance, weight, technical requirements, inspection and test as well as packaging, marking and quality certificate. It is applicable to tandem cold rolling low-carbon steel sheet and strip (hereinafter referred to as steel sheet and strip) with thickness of 0.30mm to 3.5mm produced by Baoshan Iron and Steel Co., Ltd. 2 Normative References The following documents contain provisions which, through reference in this standard, constitute provisions of this standard. For dated reference, subsequent amendments (excluding corrections) to, or revisions, of any of these publications do not apply to this standard. However, parties to agreements based on this standard are encouraged to investigate the possibility of applying the most recent editions of the standards indicated below. For undated references, the latest edition of the normative document referred to applies. GB 222-1984 Method of Sampling Steel for Determination of Chemical Composition and Permissible Variations for Product Analysis GB/T 223 Methods for Chemical Analysis of Iron, Steel and Alloy GB/T 228-2002 Metallic Materials - Tensile Testing at Ambient Temperature GB/T 2975-1998 Steel and Steel Products - Location and Preparation of Test Pieces for Mechanical Testing GB/T 5027-1999 Metallic materials - Sheet and Strip: Determination of Plastic Strain Ratio (r-values) GB/T 5028-1999 Metallic Materials - Sheet and Strip: Determination of Tensile Strain Hardening Exponent (n-values) GB/T 8170-1987 Rules for Rounding off of Numerical Values Q/BQB 400-2003 Packaging, Marking and Quality Certificate of Cold-rolled Products Q/BQB 401-2003 Dimension, Appearance, Weight and Tolerance of Tandem Cold Rolling Cold-rolled Steel Sheets and Strips SAE J911-1998 Method for Measuring Surface Roughness and Peak Number of Cold-rolled Steel Sheets 3 Classification and Code 3.1 The classification of steel sheets and strips in term of the usage is in accordance with the requirements as specified in Table 1. Table 1 Designation Usage DC01 (St12) For general purpose DC03 (St13) For drawing DC04 (St14, St15) For deep drawing DC05 (BSC2) For special-deep drawing DC06 (St16, St14 –T, BSC 3) For super-deep drawing Note: The designations in parentheses can be used until the end of 2005. 3.2 The classification of steel sheets and strips in term of the surface quality is in accordance with the requirements as specified in Table 2. 3.3 The classification of steel sheets and strips in term of the surface structure is in accordance with the requirements as specified in Table 3. Table 2 Grade Code Relatively advanced finishing surface FB (O3) Advanced finishing surface FC (O4) Super-advanced finishing surface FD (O5) Table 3 Surface structure Code Dot surface D Bright surface B 4 Information Needed in Ordering 4.1 The user should provide the following information when ordering: a) product name b) the product standard number c) designation d) product specification, dimension and unevenness accuracy e) edge condition f) surface structure g) surface quality grade h) packaging mode i) usage 4.2 If information, e.g. dimension & roughness precision, surface structure, surface quality grade, edge condition and packaging mode, is not specified in the order contract, the product of this standard shall be supplied as trimmed steel sheets and strips in common dimension & roughness precision, of dot surface and Grade FB surface quality, and shall be packaged in the mode given by the Supplier. 5 Dimension, Appearance, Weight and Tolerance The dimensions, appearance, weight and tolerance of steel sheets and strips shall meet the requirements specified in Q/BQB 401. 6 Technical Requirements 6.1 Chemical composition 6.1.1 The chemical composition of the steel (melting analysis) shall meet the requirements specified in Table 4. Table 4 Designation Chemical composition % C Mn P S Alt a Ti b DC01 (St12) ≤0.10 ≤0.50 ≤0.035 ≤0.025 ≥0.020 — DC03 (St13) ≤0.08 ≤0.45 ≤0.030 ≤0.025 ≥0.020 — DC04 (St14, St15) ≤0.08 ≤0.40 ≤0.025 ≤0.020 ≥0.020 — DC05 (BSC2) ≤0.008 ≤0.30 ≤0.020 ≤0.020 ≥0.015 ≤0.20 DC06 (St16, St14 –T, BSC 3) ≤0.006 ≤0.30 ≤0.020 ≤0.020 ≥0.015 ≤0.20 a For Designations DC01, DC03 and DC04 and when C≤0.01, Alt≥0.015 . b Part of Ti may be replaced with Nb, in which case the total content of Nb and Ti is ≤0.20. 6.1.2 The tolerance of the chemical composition of the finished steel sheet and strip shall meet the requirements of GB/T 222. 6.2 Smelting method The steel used for steel sheet and strip shall be smelted in oxygen converter or electric furnace. 6.3 Delivery condition 6.3.1 After the steel sheet and strip are tandem cold-rolled, they are delivered after annealing and leveling. 6.3.2 The steel sheets and strips shall be delivered oiled, and the oil film shall be removable with aqueous alkali. Under general non-naked packaging, transportation, handling and storage conditions, the Supplier shall ensure the products to be free from rust within 6 months from the day of manufacture. As required by the Demander and noted in the contract based on the agreement of both the Supplier and the Demander, delivery in oiled state may not be adopted.

1 Scope 2 Normative References 3 Classification and Code 4 Information Needed in Ordering 5 Dimension, Appearance, Weight and Tolerance 6 Technical Requirements 7 Inspection and Test 8 Packaging, Marking and Quality Certificate 9 Rules for Rounding off of Numerical Values Annex A (Informative) Comparison Table of Similar Designations in this Standard and Adopted Standards as well as Relevant Standards Additional Explanation

寶山鋼鐵股份有限公司企業標準 冷連軋低碳鋼板及鋼帶 Q/BQB 403－2003 代替Q/BQB 403-1999 BZJ 407-1999 1 范圍 本標準規定了冷連軋低碳鋼板及鋼帶的分類和代號、尺寸、外形、重量、技術要求、檢驗和試驗、包裝、標志及質量證明書等。 本標準適用于寶山鋼鐵股份有限公司生產的厚度為0.30mm～3.5mm的冷連軋低碳鋼板及鋼帶（以下簡稱鋼板及鋼帶）。 2 規范性引用文件 下列文件中的條款通過本標準的引用而成為本標準的條款。凡是注日期的引用文件，其隨后所有的修改單（不包括勘誤的內容）或修訂版均不適用于本標準，然而，鼓勵根據本標準達成協議的各方研究是否可使用這些文件的最新版本。凡是不注日期的引用文件，其最新版本適用于本標準。 GB/T 222－1984 鋼的化學分析用試樣取樣法及成品化學成分允許偏差 GB/T 223 鋼鐵及合金化學分析方法 GB/T 228－2002 金屬材料 室溫拉伸試驗方法 GB/T 2975－1998 鋼及鋼產品力學性能試驗取樣位置及試樣制備 GB/T 5027－1999 金屬薄板和薄帶塑性應變比（r值）試驗方法 GB/T 5028－1999 金屬薄板和薄帶拉伸應變硬化指數（值）試驗方法 n GB/T 8170－1987 數值修約規則 Q/BQB 400－2003 冷軋產品的包裝、標志及質量證明書 Q/BQB 401－2003 冷連軋鋼板及鋼帶的尺寸、外形、重量及允許偏差 SAE J911－1998 冷軋鋼板表面粗糙度和峰值數測量方法 3 分類和代號 3.1 鋼板及鋼帶按用途區分如表1的規定。 表 1 牌 號 用 途 DC01（St12） 一般用 DC03（St13） 沖壓用 DC04（St14，St15） 深沖用 DC05（BSC2） 特深沖用 DC06（St16，St14 –T，BSC 3） 超深沖用 注：括號內的牌號可以使用至2005年年底。 3.2 鋼板及鋼帶按表面質量區分如表2的規定。 3.3 鋼板及鋼帶按表面結構區分如表3的規定。 表2 級 別 代 號 較高級的精整表面 FB（O3） 高級的精整表面 FC（O4） 超高級的精整表面 FD（O5） 表3 表 面 結 構 代 號 麻 面 D 光亮表面 B 4 訂貨所需信息 4.1 訂貨時用戶應提供如下信息： a) 產品名稱 b) 本產品標準號 c) 牌號 d) 產品規格及尺寸、不平度精度 e) 邊緣狀態 f) 表面結構 g) 表面質量級別 h) 包裝方式 i) 用途 4.2 如訂貨合同中未注明尺寸及不平度精度、表面結構、表面質量級別、邊緣狀態及包裝方式，則本標準產品按普通的尺寸及不平度精度、表面結構為麻面、FB級表面質量的切邊鋼帶及切邊鋼板供貨，并按供方提供的包裝方式包裝。 5 尺寸、外形、重量及允許偏差 鋼板及鋼帶的尺寸、外形、重量及允許偏差按Q/BQB 401的規定。 6 技術要求 6.1 化學成分 6.1.1 鋼的化學成分（熔煉分析）應符合表4的規定。 表4 牌 號 化 學 成 分 ％ C Mn P S Alt a Ti b DC01（St12） ≤0.10 ≤0.50 ≤0.035 ≤0.025 ≥0.020 － DC03（St13） ≤0.08 ≤0.45 ≤0.030 ≤0.025 ≥0.020 － DC04（St14，St15） ≤0.08 ≤0.40 ≤0.025 ≤0.020 ≥0.020 － DC05（BSC2） ≤0.008 ≤0.30 ≤0.020 ≤0.020 ≥0.015 ≤0.20 DC06（St16， St14 –T，BSC 3） ≤0.006 ≤0.30 ≤0.020 ≤0.020 ≥0.015 ≤0.20 a 對于牌號DC01、 DC03和 DC04，當C≤0.01時Alt≥0.015。 b 可以用Nb代替部分Ti，此時Nb和Ti的總含量≤0.20。 6.1.2鋼板及鋼帶的成品化學成分允許偏差應符合GB/T 222的規定。 6.2 冶煉方法 鋼板及鋼帶所用的鋼采用氧氣轉爐冶煉。 6.3 交貨狀態 6.3.1 鋼板及鋼帶冷連軋后經退火及平整后交貨。 6.3.2 鋼板及鋼帶通常涂油供貨，所涂油膜應能用堿水溶液除掉，供方保證自制造之日起在通常的非裸包包裝、運輸、裝卸及貯存條件下六個月不生銹。根據需方要求，經供需雙方協議并在合同中注明，亦可以不涂油供貨。 6.4 力學性能 鋼板及鋼帶的力學性能應符合表5的規定。 表 5 牌 號 屈服強度a MPa 抗拉強度 MPa 不小于 斷后伸長率 （L0=80mm，b=20mm） ％ 不小于 r值b, c 不小于 n值b, c 不小于 公稱厚度 mm <0.70 0.70～<1.0 1.0～<1.6 ≥1.6 DC01（St12） 130～260 270 28 30 32 34 － － DC03（St13） 120～240 270 32 34 35 36 － － DC04（St14，St15） 120～210 270 36 38 39 40 1.5 0.18 DC05（BSC2） 110～190 260 38 39 40 41 1.8 0.20 DC06（St16， St14 –T，BSC 3） 100～180 250 39 40 41 42 2.0 0.22 a 當屈服現象不明顯時采用RP0.2，否則采用ReL。 b 對于牌號DC04其r值、n值為r90和n90；對于牌號DC05、DC06其r值、n值為 和 。當厚度≥1.6mm時，r值允許降低0.2；當厚度≥2.0mm時，r值和n值不作保證。 c 。 6.5 拉伸應變痕 鋼板及鋼帶拉伸應變痕的規定如表6所示。 表6 牌 號 拉伸應變痕 DC01（St12） 鋼板及鋼帶在室溫條件下儲存，在制造后3個月內，保證使用時不出現拉伸應變痕 DC03（St13） 鋼板及鋼帶在室溫條件下儲存，在制造后6個月內，保證使用時不出現拉伸應變痕 DC04（St14，St15） 鋼板及鋼帶在室溫條件下儲存，在制造后6個月內，保證使用時不出現拉伸應變痕 DC05（BSC2） 鋼板及鋼帶在室溫條件下儲存，保證使用時不出現拉伸應變痕 DC06（St16， St14 –T，BSC 3） 鋼板及鋼帶在室溫條件下儲存，保證使用時不出現拉伸應變痕 6.6 表面質量 6.6.1 鋼板及鋼帶表面不得有結疤、裂紋、夾雜等對使用有害的缺陷，鋼板及鋼帶不得有分層。 6.6.2 鋼板及鋼帶各表面質量級別的特征如表7所述。 6.6.3 對于鋼帶，由于沒有機會切除帶缺陷部分，因此鋼帶允許帶缺陷交貨，但有缺陷的部分不得超過每卷總長度的6％。 表7 級 別 代 號 特 征 較高級的精整表面 FB （O3） 表面允許有少量不影響成型性及涂、鍍附著力的缺陷，如輕微的劃傷、壓痕、麻點、輥印及氧化色等。 高級的精整表面 FC （O4） 產品二面中較好的一面無肉眼可見的明顯缺欠，另一面必須至少達到FB的要求。 超高級的精整表面 FD （O5） 產品二面中較好的一面不得有任何缺欠，即不能影響涂漆后的外觀質量或電鍍后的外觀質量，另一面必須至少達到FB的要求。 6.7 表面結構 表面結構為麻面（D）時平均粗糙度Ra按0.6μm＜Ra≤1.9μm控制，表面結構為光亮表面（B）時平均粗糙度Ra按Ra≤0.9μm控制。 7 檢驗和試驗 7.1 鋼板及鋼帶的外觀用肉眼檢查。 7.2 鋼板及鋼帶的尺寸、外形應用合適的測量工具測量。 7.3 r值是在16％應變時計算得到的；n值是在10％～20％應變范圍內計算得到的，當均勻伸長率小于20％時，應變范圍為10％至均勻伸長結束。 7.4 每批鋼板及鋼帶的檢驗項目、試樣數量、取樣方法、試驗方法及取樣方向應符合表8的規定。 表 8 序號 檢驗項目 試樣數量（個） 取樣方法 試驗方法 取樣方向 1 化學分析 1/爐 GB/T 222 GB/T 223 － 2 拉伸試驗 1 GB/T 2975 GB/T 228 橫向試樣 3 塑性應變比（r值） 1或3 GB/T 5027 － 4 應變硬化指數（n值） 1或3 GB/T 5028 － 5 表面粗糙度 － SAE J911 － 注：r90、n90為一個試樣； 、 為三個試樣。 7.5 鋼板及鋼帶應按批驗收，每個檢驗批應由不大于30噸的同牌號、同規格、同加工狀態的鋼板及鋼帶組成。 7.6 對于拉伸、塑性應變比（r值）和應變硬化指數（n值）試驗，如有某一項試驗結果不符合標準要求，則從同一批中再任取雙倍數量的試樣進行該不合格項目的復驗。復驗結果（包括該項目試驗所要求的所有指標）合格，則整批合格。復驗結果（包括該項目試驗所要求的所有指標）即使有一個指標不合格，則復驗不合格。如復驗不合格，則已做試驗且試驗結果不合的單件不能驗收，但該批材料中未做試驗的單件可逐件重新提交試驗和驗收。 8 包裝、標志及質量證明書 鋼板及鋼帶的包裝、標志及質量證明書應符合Q/BQB 400的規定。如需方對包裝重量有特殊要求，應在合同中注明。 9 數值修約規則 數值修約規則應符合GB/T 8170的規定。 附錄A （資料性附錄） 本標準與采用標準及有關標準相近牌號對照表 表 A.1 標準號 Q/BQB 403-2003 EN 10130-1999 EN 10130-1991 DIN 1623-(1)-1983 GB/T5213-2001 Q/BQB 403-1999 BZJ 407-1999 牌 號 DC01（St12） DC01 FeP01 St12 － St12 DC03（St13） DC03 FeP03 RRSt13 － St13 DC04（St14，St15） DC04 FeP04 St14 SC1 St14，St14F，St14HF， St14ZF， St15 DC05（BSC2） DC05 FeP05 － SC2 BSC2 DC06（St16， St14 –T，BSC 3） DC06 FeP06 － SC3 St16，St14 –T，BSC 3 附加說明： 本標準與EN 10130-1999的一致性程度為非等效。 本標準代替Q/BQB 403-1999和BZJ 407-1999。 本標準與Q/BQB 403-1999相比主要變化如下： —— 對牌號進行了修改和整合； —— 表面質量級別由兩種修改為三種； —— 表面結構由四種修改為兩種，并增加了表面粗糙度的控制值； —— 取消St14按拉延級別分為F、HF和ZF三個級別的規定； —— 取消標記示例； —— 取消化學成分中Si和殘余元素的規定，對C、S、Alt等元素的含量進行了修改； —— 對屈服強度、抗拉強度和斷后伸長率進行了修改，取消硬度和杯突值的規定，DC04、DC05和DC06增加r值、值的規定； n —— 增加拉伸應變痕的規定； —— 鋼帶允許帶缺陷部分從8％修改為6％； —— 修改復驗的規定； —— 增加數值修約規則的規定。 本標準的附錄A為資料性附錄。 本標準由寶山鋼鐵股份有限公司制造管理部提出。 本標準由寶山鋼鐵股份有限公司制造管理部起草。 本標準起草人 徐宏偉。 本標準于1988年首次發布，1994第一次修訂，1997第二次修訂，1999第三次修訂。