Codeofchina.com is in charge of this English translation. In case of any doubt about the contents of English translation, the Chinese original shall be considered authoritative.
This standard was developed in accordance with the rules of GB/T 1.1-2009.
This standard replaces "Designation and Composition of Titanium and Titanium Alloys" (GB/T 3620.1-2007).
The following main technical changes have been made with respect to GB/T 3620.1 - 2007:
——the designation and composition of industrial unalloyed titanium in GB/T 3620.1 - 1994 are recovered;
——the designations of industrial unalloyed titanium are changed uniformly, and added with letter "G";
——the designations are listed according to the classification of titanium;
——the editorial errors of designations TA22-1, A24, TC15 and TC17 are revised;
——the content of Si in TA19 is revised;
——eight newly registered α and near α alloy designations are added, including TA29, TA30, TA31, TA32, TA33, TA34, TA35 and TA36;
——six newly registered β and near β alloy designations are added, including TB12, TB13, TB14, TB15, TB16 and TB17;
——six newly registered α-β alloy designations are added, including TC27, TC28, TC29, TC30, TC31 and TC32;
——the naming rules for titanium alloy designations are added;
——the Implementation requirements on the designation and composition of industrial unalloyed titanium are specified.
This standard is under the jurisdiction of National Technical Committee on Nonferrous Metals of Standardization Administration of China (SAC/TC 243).
The previous editions of the standard replaced by this standard are as follows:
- GB/T 3620-1983, GB/T 3620.1-1994 and GB/T 3620.1-2007.
Designation and Composition of Titanium and Titanium Alloys
1 Scope
This standard specifies the designation and composition, etc. of titanium and titanium alloy products.
This standard is applicable to various finished products and semifinished products (including ingot) made of titanium and titanium alloy through press working.
2 Normative References
The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.
GB/T 3620.2 Titanium and Titanium Alloys - Permissible Variations of Chemical Composition for Wrought Product Analysis
GB/T 4698
(All Parts) Sponge Titanium, Titanium and Titanium Alloys
GB/T 8170 Rules of Rounding Off for Numerical Values & Expression and Judgment of Limiting Values
3 Compositions
3.1 Designations and compositions
3.1.1 The designations and compositions of titanium and titanium alloy products shall meet the requirements specified in Tables 1, 2 and 3, among which Table 1 is for the those of industrial unalloyed titanium, α and near α titanium and titanium alloys; Table 2 is for those of β and near β; Table 3 is for those of α-β titanium alloy.
3.1.2 Boron shall be added according to its nominal amount, and the measured data shall be reported for reference.
3.1.3 When only upper limit is specified for Si in Tables 1, 2 and 3, Si shall be controlled as an impurity element.
3.2 Other elements
3.2.1 Other elements refer to the inherent microelements during production process of titanium and titanium alloys, rather than elements added artificially.
3.2.2 Generally, other elements include Al, V, Sn, Mo, Cr, Mn, Zr, Ni, Cu, Si and Y (alloy elements in the designation shall be removed). The content of Y shall not be larger than 0.005%. Other special requirements requested by users, if any, shall be determined through negotiation between both parties and then noted in the contract.
3.2.3 The supplier may not inspect other elements when the products leave factory, and may conduct sampling inspection if required and noted by the user in the contract.
3.3 Composition tolerance
When the demander takes samples from the products for check analysis on the composition, the composition tolerance shall meet the requirements of GB/T 3620.2.
4 Composition Analysis and Analysis Report
4.1 The arbitrary analysis on composition of titanium and titanium alloy products shall be conducted according to GB/T 4698, while routine inspection may be conducted according to ICP or other approved methods.
4.2 Unless otherwise stated in the product standard, the supplier may take samples from titanium and titanium alloy ingot (from finished product in case of hydrogen element) for composition analysis of the product.
4.3 The composition of titanium and titanium alloy products is allowed to be subjected to second analysis, the result of which will be regarded as the final judgment basis.
4.4 The significant digits of the analysis values in the composition analysis report shall be consistent with those of corresponding limit values of corresponding designations in this standard. The numbers after significant digits shall be rounded off according to the rules of GB/T 8170.
5 Others
5.1 See Annex A for the designation and composition of titanium and titanium alloys deleted in the revision of GB/T 3620.1.
5.2 See Annex B for the corresponding relationship between industrial unalloyed titanium and unalloyed titanium designations in ASTM standard system in Table 2 .
5.3 See Annex C for the naming rules for designations of titanium and titanium alloy.
5.4 See Annex D for all designation and composition of industrial unalloyed titanium in this standard as well as the implementation description of relevant product standards.
Foreword i
1 Scope
2 Normative References
3 Compositions
4 Composition Analysis and Analysis Report
5 Others
Annex A (Informative) Designations and Compositions of Titanium Alloys Deleted
Annex B (Informative) Corresponding Relationship between Industrially Unalloyed Titanium in Table 2 of this Standard and the Designations of Unalloyed Titanium in ASTM Standard System
Annex C (Normative) Naming Rules for Titanium and Titanium Alloy Designations
Annex D (Informative) Statement on Implementation of this Standard and Relevant Standards
ICS 77.120.50
H 64
中華人民共和國(guó)國(guó)家標(biāo)準(zhǔn)
GB/T 3620.1—2016
代替GB/T 3620.1—2007
鈦及鈦合金牌號(hào)和化學(xué)成分
Designation and composition of titanium and titanium alloys
2016-12-30發(fā)布 2017-11-01實(shí)施
中華人民共和國(guó)國(guó)家質(zhì)量監(jiān)督檢驗(yàn)檢疫總局
中國(guó)國(guó)家標(biāo)準(zhǔn)化管理委員會(huì)
發(fā)布
前言
本標(biāo)準(zhǔn)按照GB/T 1.1—2009給出的規(guī)則起草。
本標(biāo)準(zhǔn)代替GB/T 3620.1—2007《鈦及鈦合金牌號(hào)和化學(xué)成分》。
本標(biāo)準(zhǔn)與GB/T 3620.1—2007相比，主要技術(shù)內(nèi)容變化如下：
——恢復(fù)了GB/T 3620.1—1994中工業(yè)純鈦的牌號(hào)和化學(xué)成分；
——將工業(yè)純鈦牌號(hào)統(tǒng)一進(jìn)行變更，在工業(yè)純鈦牌號(hào)后增加“G”字母；
——將牌號(hào)按鈦的分類方式分別列表規(guī)范；
——修訂了TA22-1、TA24、TC15、TC17牌號(hào)的編輯錯(cuò)誤；
——修訂了TA19中的Si含量；
——增加了TA29、TA30、TA31、TA32、TA33、TA34、TA35和TA36共計(jì)8個(gè)新注冊(cè)α型和近α型合金牌號(hào)；
——增加了TB12、TB13、TB14、TB15、TB16和TB17共計(jì)6個(gè)新注冊(cè)β型和近β型合金牌號(hào)；
——增加了TC27、TC28、TC29、TC30、TC31和TC32共計(jì)6個(gè)新注冊(cè)α-β型合金牌號(hào)；
——增加了鈦合金牌號(hào)命名規(guī)則；
——規(guī)定了工業(yè)純鈦牌號(hào)和化學(xué)成分實(shí)施要求。
本標(biāo)準(zhǔn)由全國(guó)有色金屬標(biāo)準(zhǔn)化技術(shù)委員會(huì)(SAC/TC 243)歸口。
本標(biāo)準(zhǔn)負(fù)責(zé)起草單位：寶鈦集團(tuán)有限公司、寶雞鈦業(yè)股份有限公司、中國(guó)有色金屬工業(yè)標(biāo)準(zhǔn)計(jì)量質(zhì)量研究所。
本標(biāo)準(zhǔn)參加起草單位：北京航空材料研究院、西部金屬材料股份有限公司、航天材料及工藝研究所、中國(guó)船舶重工集團(tuán)公司第七二五研究所、中鋁沈陽(yáng)有色金屬加工有限公司、北京有色金屬研究總院、湖南金天鈦業(yè)科技有限公司。
本標(biāo)準(zhǔn)主要起草人：馮軍寧、喬璐、馬忠賢、胡志杰、陳峰、王儉、李獻(xiàn)軍、劉東升、張宇瑋、慶達(dá)嘎、王洋、王麗、彭暉、魏衍廣。
本標(biāo)準(zhǔn)所代替標(biāo)準(zhǔn)的歷次版本發(fā)布情況為：
——GB/T 3620—1983、GB/T 3620.1—1994、GB/T 3620.1—2007。
鈦及鈦合金牌號(hào)和化學(xué)成分
1 范圍
本標(biāo)準(zhǔn)規(guī)定了鈦及鈦合金產(chǎn)品的牌號(hào)、化學(xué)成分等。
本標(biāo)準(zhǔn)適用于鈦及鈦合金壓力加工的各種成品和半成品(包括鑄錠)。
2規(guī)范性引用文件
下列文件對(duì)于本文件的應(yīng)用是必不可少的。凡是注日期的引用文件，僅注日期的版本適用于本文件。凡是不注日期的引用文件，其最新版本(包括所有的修改單)適用于本文件。
GB/T 3620.2鈦及鈦合金加工產(chǎn)品化學(xué)成分允許偏差
GB/T 4698(所有部分) 海綿鈦、鈦及鈦合金化學(xué)分析方法
GB/T 8170數(shù)值修約規(guī)則與極限數(shù)值的表示和判定
3化學(xué)成分
3.1牌號(hào)與化學(xué)成分
3.1.1鈦及鈦合金產(chǎn)品的牌號(hào)和化學(xué)成分應(yīng)符合表1、表2和表3的規(guī)定。其中表1為工業(yè)純鈦、α型和近α型鈦及鈦合金牌號(hào)和化學(xué)成分；表2為β型和近β型鈦合金牌號(hào)及化學(xué)成分；表3為α-β型鈦合金牌號(hào)及化學(xué)成分。
3.1.2硼按名義量加入，并報(bào)實(shí)測(cè)數(shù)據(jù)，供參考。
3.1.3表1、表2和表3中Si元素僅規(guī)定上限值時(shí)，應(yīng)作為雜質(zhì)元素控制。
3.2 其他元素
3.2.1其他元素是指在鈦及鈦合金生產(chǎn)過(guò)程中固有存在的微量元素，而不是人為添加的元素。
3.2.2 其他元素一般包括：Al、V、Sn、Mo、Cr、Mn、Zr、Ni、Cu、Si、Y(該牌號(hào)中含有的合金元素應(yīng)除去)。Y含量為不大于0.005％。用戶有其他特殊要求時(shí)，應(yīng)經(jīng)雙方協(xié)商，并在合同中注明。
3.2.3產(chǎn)品出廠時(shí)供方可不檢驗(yàn)其他元素，用戶要求并在合同中注明時(shí)可予以抽檢。
3.3成分允許偏差
需方從產(chǎn)品上取樣進(jìn)行化學(xué)成分復(fù)驗(yàn)分析時(shí)，其成分允許偏差應(yīng)符合GB/T 3620.2的規(guī)定。
4化學(xué)成分分析和分析報(bào)告
4.1鈦及鈦合金產(chǎn)品化學(xué)成分仲裁分析按GB/T 4698進(jìn)行，常規(guī)檢驗(yàn)可按ICP或認(rèn)可的其他方法進(jìn)行。
4.2除產(chǎn)品標(biāo)準(zhǔn)另有規(guī)定外，供方均可在鈦及鈦合金鑄錠上(氫元素在成品上)取樣進(jìn)行產(chǎn)品的化學(xué)成分分析。
4.3鈦及鈦合金產(chǎn)品的化學(xué)成分允許做第二次分析，并以第二次的分析結(jié)果為最終判定依據(jù)。
4.4化學(xué)成分分析報(bào)告中的分析數(shù)值，其有效位數(shù)應(yīng)與本標(biāo)準(zhǔn)中對(duì)應(yīng)牌號(hào)的相應(yīng)界限數(shù)值的有效位數(shù)一致。有效位數(shù)后面的數(shù)字應(yīng)按GB/T 8170規(guī)定的規(guī)則進(jìn)行修約。
5其他
5.1 附錄A為歷次GB/T 3620.1修訂時(shí)刪除的鈦及鈦合金牌號(hào)和化學(xué)成分。
5.2 表2中工業(yè)純鈦與ASTM標(biāo)準(zhǔn)體系中純鈦牌號(hào)的對(duì)應(yīng)關(guān)系參見附錄B。
5.3附錄C給出了鈦及鈦合金牌號(hào)命名規(guī)則。
5.4本標(biāo)準(zhǔn)中涉及的所有工業(yè)純鈦牌號(hào)和化學(xué)成分與相關(guān)產(chǎn)品標(biāo)準(zhǔn)的執(zhí)行說(shuō)明參見附錄D。
表1 工業(yè)純鈦、α型和近α型鈦及鈦合金牌號(hào)和化學(xué)成分
合金
牌號(hào) 名義化學(xué)成分 化學(xué)成分(質(zhì)量分?jǐn)?shù))/％
主要成分 雜質(zhì)，不大于
Ti Al Si V Mn Fe Ni Cu Zr Nb Mo Ru Pd Sn Ta Nd Fe C N H O 其他元素
單一 總和
TA0 工業(yè)純鈦 余量 — — — — — — — — — — — — — — — 0.15 0.10 0.03 0.015 0.15 0.1 0.4
TA1 工業(yè)純鈦 余量 — — — — — — — — — — — — — — — 0.25 0.10 0.03 0.015 0.20 0.1 0.4
TA2 工業(yè)純鈦 余量 — — — — — — — — — — — — — — — 0.30 0.10 0.05 0.015 0.25 0.1 0.4
TA3 工業(yè)純鈦 余量 — — — — — — — — — — — — — — — 0.40 0.10 0.05 0.015 0.30 0.1 0.4
TA1GELI 工業(yè)純鈦 余量 — — — — — — — — — — — — — — — 0.10 0.03 0.012 0.008 0.10 0.05 0.20
TA1G 工業(yè)純鈦 余量 — — — — — — — — — — — — — — — 0.20 0.08 0.03 0.015 0.18 0.10 0.40
TA1G-1 工業(yè)純鈦 余量 ≤0.20 ≤0.08 — — — — — — — — — — — — — 0.15 0.05 0.03 0.003 0.12 — 0.10
TA2GELI 工業(yè)純鈦 余量 — — — — — — — — — — — — — — — 0.20 0.05 0.03 0.008 0.10 0.05 0.20
TA2G 工業(yè)純鈦 余量 — — — — — — — — — — — — — — — 0.30 0.08 0.03 0.015 0.25 0.10 0.40
TA3GELI 工業(yè)純鈦 余量 — — — — — — — — — — — — — — — 0.25 0.05 0.04 0.008 0.18 0.05 0.20
TA3G 工業(yè)純鈦 余量 — — — — — — — — — — — — — — — 0.30 0.08 0.05 0.015 0.35 0.10 0.40
TA4GELI 工業(yè)純鈦 余量 — — — — — — — — — — — — — — — 0.30 0.05 0.05 0.008 0.25 0.05 0.20
TA4G 工業(yè)純鈦 余量 — — — — — — — — — — — — — — — 0.50 0.08 0.05 0.015 0.40 0.10 0.40
TA5 Ti-4Al-0.005B 余量 3.3～4.7 — — — — — — — — — B:0.005 — — — — 0.30 0.08 0.04 0.015 0.15 0.10 0.40
TA6 Ti-5Al 余量 4.0～5.5 — — — — — — — — — — — — — — 0.30 0.08 0.05 0.015 0.15 0.10 0.40
TA7 Ti-5Al-2.5Sn 余量 4.0～6.0 — — — — — — — — — — — 2.0～3.0 — — 0.50 0.08 0.05 0.015 0.20 0.10 0.4
TA7ELIa Ti-5Al-2.5SnELI 余量 4.50～5.75 — — — — — — — — — — — 2.0～3.0 — — 0.25 0.05 0.035 0.012 5 0.12 0.05 0.30
TA8 Ti-0.05Pd 余量 — — — — — — — — — — — 0.04～0.08 — — — 0.30 0.08 0.03 0.015 0.25 0.10 0.40
TA8-1 Ti-0.05Pd 余量 — — — — — — — — — — — 0.04～0.08 — — — 0.20 0.08 0.03 0.015 0.18 0.10 0.40
TA9 Ti-0.2Pd 余量 — — — — — — — — — — — 0.12～0.25 — — — 0.30 0.08 0.03 0.015 0.25 0.10 0.40
TA9-1 Ti-0.2Pd 余量 — — — — — — — — — — — 0.12～0.25 — — — 0.20 0.08 0.03 0.015 0.18 0.10 0.40
TA10 Ti-0.3Mo-0.8Ni 余量 — — — — — 0.6～0.9 — — — 0.2～0.4 — — — — — 0.30 0.08 0.03 0.015 0.25 0.10 0.40
TA11 Ti-8Al-1Mo-1V 余量 7.35～8.35 — 0.75～1.25 — — — — — — 0.75～1.25 — — — — — 0.30 0.08 0.05 0.015 0.12 0.10 0.30
TA12 Ti-5.5Al-4Sn-2Zr-1Mo-1Nd-0.25Si 余量 4.8～6.0 0.2～0.35 — — — — — 1.5～2.5 — 0.75～1.25 — — 3.7～4.7 — 0.6～1.2 0 25 0.08 0.05 0.012 5 0.15 0.10 0.40
TA12-1 Ti-5Al-4Sn-2Zr-1Mo-1Nd-0.25Si 余量 4.5～5.5 0.2～0.35 — — — — — 1.5～2.5 — 1.0～2.0 — — 3.7～4.7 — 0.6～1.2 0.25 0.08 0.04 0.012 5 0.15 0.10 0.30
TA13 Ti-2.5Cu 余量 — — — — — — 2.0～3.0 — — — — — — — — 0.20 0.08 0.05 0.010 0.20 0.10 0.30
TA14 Ti-2,3Al-11Sn-5Zr-1Mo-0.2Si 余量 2.0～2.5 0.10～0.50 — — — — — 4.0～6 0 — 0.8～1.2 — — 10.52～11.50 — — 0.20 0.08 0.05 0.012 5 0.20 0.10 0.30
TA15 Ti-6.5Al-1Mo-1V-2Zr 余量 5.5～7.1 ≤0.15 0.8～2.5 — — — — 1.5～2.5 — 0.5～2.0 — — — — — 0.25 0.08 0.05 0.015 0.15 0.10 0.30
TA15-1 Ti-2.5Al-1Mo-1V-1.5Zr 余量 2.0～3.0 ≤0.10 0.5～1.5 — — — — 1.0～2.0 — 0.5～1.5 — — — — — 0.15 0.05 0.04 0.003 0.12 0.10 0.30
TA15-2 Ti-4Al-1Mo-1V-1.5Zr 余量 3.5～4.5 ≤0.10 0.5～1.5 — — — — 1.0～2.0 — 0.5～1.5 — — — — — 0.15 0.05 0.04 0.003 0.12 0.10 0.30
TA16 Ti-2Al-2.5Zr 余量 1.8～2.5 ≤0.12 — — — — — 2.0～3.0 — — — — — — — 0.25 0.08 0.04 0.006 0.15 0.10 0.30
TA17 Ti-4Al-2V 余量 3.5～4.5 ≤0.15 1.5～3.0 — — — — — — — — — — — — 0.25 0.08 0.05 0.015 0.15 0.10 0.30
TA18 Ti-3Al-2.5V 余量 2.0～3.5 — 1.5～3.0 — — — — — — — — — — — — 0.25 0.08 0.05 0.015 0.12 0.10 0.30
TA19 Ti-6Al-2Sn-4Zr-2Mo-0.08Si 余量 5.5～6.5 0.06～0.10 — — — — — 3.6～4.4 — 1.8～2.2 — — 1.8～2.2 — — 0.25 0.05 0.05 0.012 5 0.15 0.10 0.30
TA20 Ti-4Al-3V-1.5Zr 余量 3.5～4.5 ≤0.10 2.5～3.5 — — — — 1.0～2.0 — — — — — — — 0.15 0.05 0.04 0.003 0.12 0.10 0.30
表1(續(xù))
合金
牌號(hào) 名義化學(xué)成分 化學(xué)成分(質(zhì)量分?jǐn)?shù))/％
主要成分 雜質(zhì)，不大于
Ti Al Si V Mn Fe Ni Cu Zr Nb Mo Ru Pd Sn Ta Nd Fe C N H O 其他元素
單一 總和
TA21 Ti-1Al-1Mn 余量 0.4～1.5 ≤0.12 — 0.5～1.3 — — — ≤0.30 — — — — — — — 0.30 0.10 0.05 0.012 0.15 0.10 0.30
TA22 Ti-3Al-Mo-1Ni-1Zr 余量 2.5～3.5 ≤0.15 — — — 0.3～1.0 — 0.8～2.0 — 0.5～1.5 — — — — — 0.20 0.10 0.05 0.015 0.15 0.10 0.30
TA22-1 Ti-2.5Al-1Mo-1Ni-1Zr 余量 2.0～3.0 ≤0.04 — — — 0.3～0.8 — 0.5～1.0 — 0.2～0.8 — — — — — 0.20 0.10 0.04 0.008 0.10 0.10 0.30
TA23 Ti-2.5Al-2Zr-1Fe 余量 2.2～3.0 ≤0.15 — — 0.8～1.2 — — 1.7～2.3 — — — — — — — — 0.10 0.04 0.010 0.15 0.10 0.30
TA23-1 Ti-2.5Al-2Zr-1Fe 余量 2.2～3.0 ≤0.10 — — 0.8～1.1 — — 1.7～2.3 — — — — — — — — 0.10 0.04 0.008 0.10 0.10 0.30
TA24 Ti-3Al-2Mo-2Zr 余量 2.0～3.8 ≤0.15 — — — — — 1.0～3.0 — 1.0～2.5 — — — — — 0.30 0.10 0.05 0.015 0.15 0.10 0.30
TA24-1 Ti-3Al-2Mo-2Zr 余量 1.5～2.5 ≤0.04 — — — — — 1.0～3.0 — 1.0～2.0 — — — — — 0.13 0.10 0.04 0.010 0.10 0.10 0.30
TA25 Ti-3Al-2.5V-0.05Pd 余量 2.5～3.5 — 2.0～3.0 — — — — — — — — 0.04～0.08 — — — 0.25 0.08 0.03 0.015 0.15 0.10 0.40
TA26 Ti-3Al-2.5V-0.10Ru 余量 2.5～3.5 — 2.0～3.0 — — — — — — — 0.08～0.14 — — — — 0 25 0.08 0.03 0.015 0.15 0.10 0.40
TA27 Ti-0.10Ru 余量 — — — — — — — — — — 0.08～0.14 — — — — 0.30 0.08 0.03 0.015 0.23 0.10 0.40
TA27-1 Ti-0.10Ru 余量 — — — — — — — — — — 0.08～0.14 — — — — 0.20 0.08 0.03 0.015 0.18 0.10 0.40
TA28 Ti-3Al 余量 2.0～3.0 — — — — — — — — — — — — — — 0.30 0.08 0.05 0.015 0.15 0.10 0.40
TA29 Ti-5.8Al-4Sn-4Zr-0.7Nb-1.5Ta-0.4Si-0.06C 余量 5.4～6.1 0.34～0.45 — — — — — 3.7～4.3 0.3～0.9 — — — S.7～4.3 1.3～1 7 — 0.05 0.04～0.08 0.02 0.010 0.10 0.10 0.20
TA30 Ti-5.5Al-3.5Sn-3Zr-1Nb-1Mo-0.3Si 余量 4.7～6.0 0.20～0.35 — — — — — 2.4～3.5 0.7～1.3 0.7～1.3 — — 3.0～3.8 — — 0.15 0.10 0.04 0.012 0.15 0.10 0.30
TA31 Ti-6Al-3Nb-2Zr-1Mo 余量 5.5～6.5 ≤0.15 — — — — — 1.5～2.5 2.5～3.5 0.6～1.5 — — — — — 0.25 0.10 0.05 0.015 0.15 0.10 0.30
TA32 Ti-5.5Al-3.5Sn-3Zr-1Mo-0.5Nb-0.7Ta-0.3Si 余量 5.0～6.0 0.1～0.5 — — — — — 2.5～3.5 0.2～0.7 0.3～1.6 — — 3.0～4.0 0.2～0 7 — 0.25 0.10 0.05 0.012 0.15 0,10 0.30
TA33 Ti-5.8Al-4Sn-3.5Zr-0.7Mo-0.5Nb-1.1Ta-0.4Si-0.06C 余量 5.2～6.5 0.2～0.6 — — — — — 2.5～4.0 0.2～0.7 0.2～1.0 — — 3.0～4.5 0.7～1.5 — 0.25 0.04～0.08 0.05 0.012 0.15 0.10 0.20
TA34 Ti-2Al-3.8Zr-1Mo 余量 1.0～3.0 — — — — — — 3.0～4.5 — 0.5～1.5 — — — — — 0.25 0.05 0.035 0.008 0.10 0.10 0.25
TA35 Ti-6Al-2Sn-4Zr-2Nb-1Mo-0.2Si 余量 5.8～7.0 0.05～0.50 — — — — — 3.5～4.5 1.5～2.5 0.3～1.3 — — 1.5～2.5 — — 0.20 0.10 0.05 0.015 0.15 0.10 0.30
TA36 Ti-1Al-1Fe 余量 0.7～1.3 — — — 1.0～1.4 — — — — — — — — — — — 0.10 0.05 0.015 0.15 0.10 0.30
注：TA0、TA1、TA2和TA3是恢復(fù)了GB/T 3620.1—1994中的工業(yè)純鈦牌號(hào)，化學(xué)成分與GB/T 3620.1—1994完全等同。
a TA7ELI牌號(hào)的雜質(zhì)“Fe+O”的質(zhì)量分?jǐn)?shù)總和應(yīng)不大于0.32％。
表2 β型和近β型鈦合金牌號(hào)及化學(xué)成分
合金
牌號(hào) 名義化學(xué)成分 化學(xué)成分(質(zhì)量分?jǐn)?shù))/％
主要成分 雜質(zhì)，不大于
Ti Al Si V Cr Fe 2r Nb Mo Pd Sn Fe C N H O 其他元素
單一 總和
TB2 Ti-5Mo-5V-8Cr-3Ai 余量 2.5～3.5 — 4.7～5.7 7.5～8.5 — — — 4.7～5.7 — — 0.30 0.05 0.04 0.015 0.15 0.10 0.40
TB3 Ti-3.5Al-10Mo-8V-1Fe 余量 2.7～3.7 — 7.5～8.5 — 0.8～1.2 — — 9.5～11.0 — — w 0.05 0.04 0.015 0.15 0.10 0.40
TB4 Ti-4Al-7Mo-10V-2Fe-1Zr 余量 3.0～4.5 — 9.0～10.5 — 1.5～2.5 0.5～1.5 — 6.0～7.8 — — — 0.05 0.04 0.015 0.20 0.10 0.40
表2(續(xù))
合金
牌號(hào) 名義化學(xué)成分 化學(xué)成分(質(zhì)量分?jǐn)?shù))/％
主要成分 雜質(zhì)，不大干
Ti Al Si V Cr Fe Zr Nb Mo Pd Sn Fe C N H O 其他元素
單一 總和
TB5 Ti-15V-3Al-3Cr-3Sn 余量 2.5～3.5 — 14.0～16.0 2.5～3.5 — — — — — 2.5～3.5 0.25 0.05 0.05 0.015 0.15 0.10 0.30
TB6 Ti-10V-2Fe-3Al 余量 2.6～3.4 — 9.0～11.0 — 1.6～2.2 — — — — — — 0.05 0 05 0.012 5 0.13 0.10 0.30
TB7 Ti-32Mo 余量 — — — — — — — 30.0～34.0 — — 0.30 0.08 0.05 0.015 0.20 0.10 0.40
TB8 Ti-15Mo-3Al-2.7Nb-0.25Si 余量 2.5～3.5 0.15～0.25 — — — — 2.4～3.2 14.0～16.0 — — 0.40 0.05 0.05 0.015 0.17 0.10 0.40
TB9 Ti-3Al-8V-6Cr-4Mo-4Zr 余量 3.0～4.0 — 7.5～8.5 5.5～6.5 — 3.5～4.5 — 3.5～4.5 ≤0.10 — 0.30 0.05 0.03 0.030 0.14 0.10 0.40
TB10 Ti-5Mo-5V-2Cr-3Al 余量 2.5～3.5 — 4.5～5.5 1.5～2.5 — — — 4.5～5.5 — — 0.30 0.05 0.04 0.015 0.15 0.10 0.40
TB11 Ti-15Mo 余量 — — — — — — — 14.0～16.0 — — 0.10 0.10 0.05 0.015 0.20 0.10 0.40
TB12 Ti-25V-15Cr-0.3Si 余量 — 0.2～0.5 24.0～28.0 13.0～17.0 — — — — — — 0.25 0.10 0.03 0.015 0.15 0.10 0.30
TB13 Ti-4Al-22V 余量 3 0～4.5 — 20.0～23.0 — — — — — — — 0.15 0.05 0.03 0.010 0.18 0.10 0.40
TB14a Ti-45Nb 余量 — ≤0.03 — ≤0.02 — — 42.0～47.0 — — — 0.03 0.04 0.03 0.003 5 0.16 0.10 0.30
TB15 Ti-4Al-5V-6Cr-5Mo 余量 3.5～4.5 — 4.5～5.5 5.0～6.5 — — — 4.5～5.5 — — 0.30 0.10 0.05 0.015 0.15 0.10 0.30
TB16 Ti-3Al-5V-6Cr-5Mo 余量 2.5～3.5 — 4.5～5.7 5.5～6.5 — — — 4.5～5.7 — — 0.30 0.05 0.04 0.015 0.15 0.10 0.40
TB17 Ti-6.5Mo-2.5Cr-2V-2Nb-1Sn-1Zr-4Al 余量 3.5～5.5 ≤0.15 1.0～3.0 2.0～3.5 — 0.5～2.5 1.5～3 0 5.0～7.5 — 0.5～2.5 0.15 0.08 0.05 0.015 0.13 0.10 0.40
a TB14鈦合金的Mg的質(zhì)量分?jǐn)?shù)≤0.01％，Mn的質(zhì)量分?jǐn)?shù)≤0.01％。
表3 α-β型鈦合金牌號(hào)及化學(xué)成分
合金
牌號(hào) 名義化學(xué)成分 化學(xué)成分(質(zhì)量分?jǐn)?shù))/％
主要成分 雜質(zhì)，不大于
Ti Al Si V Cr Mn Fe Cu Zr Nb Mo Ru Pd Sn Ta W Fe C N H O 其他元素
單一 總和
TC1 Ti-2Al-1.5Mn 余量 1.0～2.5 — — — 0 7～2.0 — — — — — — — — — — 0.30 0.08 0.05 0.012 0.15 0.10 0.40
TC2 Ti-4Al-1.5Mn 余量 3.5～5.0 — — — 0.8～2.0 — — — — — — — — — — 0.30 0.08 0.05 0.012 0.15 0.10 0.40
TC3 Ti-5Al-4V 余量 4.5～6.0 — 3.5～4.5 — — — — — — — — — — — — 0.30 0.08 0.05 0.015 0.15 0.10 0.40
TC4 Ti-6Al-4V 余量 5.50～6.75 — 3.5～4.5 — — — — — — — — — — — — 0.30 0.08 0.05 0.015 0.20 0.10 0.40
TC4ELI Ti-6Al-4VELI 余量 5.5～6.5 — 3.5～4.5 — — — — — — — — — — — — 0.25 0.08 0.03 0.012 0.13 0.10 0.30
TC6 Ti-6Al-1.5Cr-2.5Mo-0.5Fe-0.3Si 余量 5.5～7.0 0.15～0.40 — 0.8～2.3 — 0.2～0.7 — — — 2.0～3.0 — — — — — — 0.08 0.05 0.015 0.18 0.10 0.40
TC8 Ti-6.5Al-3.SMo-0.25Si 余量 5.8～6.8 0.20～0.35 — — — — — — — 2.8～3.8 — — — — — 0.40 0.08 0.05 0.015 0.15 0.10 0.40
TC9 Ti-6.5Al-3.5Mo-2.5Sn-0.3Si 余量 5.8～6.8 0.2～0.4 — — — — — — — 2.8～3.8 — — 1.8～2.8 — — 0.40 0.08 0.05 0.015 0.15 0.10 0.40
TC10 Ti-6Al-6V-2Sn-0.5Cu-0.5Fe 余量 5.5～6.5 — 5.5～6.5 — — 0.35～1.00 0.35～1.00 — — — — — 1.5～2.5 — — — 0.08 0.04 0.015 0.20 0.10 0.40
TC11 Ti-6.5Al-3.5Mo-1.5Zr-0.3Si 余量 5 8～7.0 0.20～0.35 — — — — — 0.8～2.0 — 2.8～3.8 — — — — — 0.25 0.08 0.05 0.012 0.15 0.10 0.40
TC12 Ti-5Al-4Mo-4Cr-2Zr-2Sn-1Nb 余量 4 5～5.5 — — 3.5～4.5 — — — 1.5～3.0 0.5～1.5 3.5～4.5 — — 1.5～2.5 — — 0.30 0.08 0.05 0.015 0.20 0.10 0.40
TC15 Ti-5Al-2.5Fe 余量 4.5～5.5 — — — — 2.0～3.0 — — — — — — — — — — 0.08 0.05 0.013 0.20 0.10 0.40
TC16 Ti-3Al-5Mo-4.5V 余量 2.2～3.8 ≤0.15 4.0～5.0 — — — — — — 4.5～5.5 — — — — — 0.25 0.08 0.05 0.012 0.15 0.10 0.30
表3(續(xù))
合金
牌號(hào) 名義化學(xué)成分 化學(xué)成分(質(zhì)量分散)/％
主要成分 雜質(zhì)，不大于
Ti Al Si V Cr Mn Fe Cu Zr Nb Mo Ru Pd Sn Ta W Fe C N H O 其他元素
單一 總和
TC17 Ti-5Al-2Sn-2Zr-4Mo-4Cr 余量 4.5～5.5 — — 3.5～4.5 — — — 1.5～2.5 — 3.5～4.5 — — 1.5～2.5 — — 0.25 0.05 0.05 0.012 5 0.08～0.13 0.10 0.30
TC18 Ti-5Al-4.75Mo-4.75V-1Cr-1Fe 余量 4.4～5.7 ≤0.15 4.0～5.5 0.5～1.5 — 0.5～1.5 — ≤0.30 — 4.0～5.5 — — — — — — 0.08 0.05 0.015 0.18 0.10 0.30
TC19 Ti-6Al-2Sn-4Zr-6Mo 余量 5.5～6.5 — — — — — — 3.5～4.5 — 5.5～6.5 — — 1.75～2.25 — — 0.15 0.04 0.04 0.012 5 0.15 0.10 0.40
TC20 Ti-6Al-7Nb 余量 5.5～6.5 — — — — — — — 6.5～7.5 — — — — ≤0.5 — 0.25 0.08 0.05 0.009 0.20 0.10 0.40
TC21 Ti-6Al-2Mo-2Nb-2Zr-2Sn-1.5Cr 余量 5.2～6.8 — — 0.9～2.0 — — — 1.6～2.5 1.7～2.3 2.2～3.3 — — 1.6～2.5 — — 0.15 0.08 0.05 0.015 0.15 0.10 0.40
TC22 Ti-6Al-4V-0.05Pd 余量 5.50～6.75 — 3.5～4.5 — — — — — — — — 0.04～0.08 — — — 0.40 0.08 0.05 0.015 0.20 0.10 0.40
TC23 Ti-6Al-4V-0.1Ru 余量 5.50～6.75 — 3.5～4.5 — — — — — — — 0.08～0.14 — — — — 0.25 0.08 0.05 0.015 0.13 0.10 0.40
TC24 Ti-4.5Al-3V-2Mo-2Fe 余量 4.0～5.0 — 2.5～3.5 — — 1.7～2.3 — — — 1.8～2.2 — — — — — — 0.05 0.05 0.010 0.15 0.10 0.40
TC25 Ti-6.5Al-2Mo-1Zr-1Sn-1W-0.2Si 余量 6.2～7.2 0.10～0.25 — — — — — 0.8～2.5 — 1.5～2.5 — — 0.8～2.5 — 0.5～1.5 0.15 0.10 0.04 0.012 0.15 0.10 0.30
TC26 Ti-13Nb-13Zr 余量 — — — — — — — 12.5～14.0 12.5～14.0 — — — — — — 0.25 0.08 0.05 0.012 0.15 0.10 0.40
TC27 Ti-5Al-4Mo-6V-2Nb-1Fe 余量 5.0～6.2 — 5.5～6.5 — — 0.5～1.5 — — 1.5～2.5 3.5～4.5 — — — — — — 0.05 0.05 0.015 0.13 0.10 0.30
TC28 Ti-6.5Al-1Mo-1Fe 余量 5.0～8.0 — — — — 0.5～2.0 — — — 0.2～2.0 — — — — — — 0.10 — 0.015 0.15 0.10
TC29 Ti-4.5Al-7Mo-2Fe 余量 3.5～5.5 ≤0.5 — — — 0.8～3.0 — — — 6.0～8.0 — — — — — — 0.10 — 0.015 0.15 0.10 0.40
TC30 Ti-5Al-3Mo-1V 余量 3.5～6.3 ≤0.15 0.9～1.9 — — — — ≤0.30 — 2.5～3.8 — — — — — 0.30 0.10 0.05 0.015 0.15 0.10 0.30
TC31 Ti-6.5Al-3Sn-3Zr-3Nb-3Mo-1W-0.2Si 余量 6.0～7.2 0.1～0.5 — — — — — 2.5～3.2 1.0～3.2 1.0～3.2 — — 2.5～3.2 — 0.3～1.2 0.25 0.10 0.05 0.015 0.15 0.10
TC32 Ti-5Al-3Mo-3Cr-1Zr-0.15Si 余量 4.5～5.5 0.1～0.2 — 2.5～3.5 — — — 0.5～1.5 — 2.5～3.5 — — — — — 0.30 0.08 0.05 0.012 5 0.20 0.10 0.40
附 錄 A
(資料性附錄)
刪除的鈦及鈦合金牌號(hào)和化學(xué)成分
刪除的鈦及鈦合金牌號(hào)和化學(xué)成分見表A.1。
表A.1 刪除的鈦及鈦合金牌號(hào)和化學(xué)成分
合金
牌號(hào) 名義化學(xué)成分 化學(xué)成分(質(zhì)量分?jǐn)?shù))/％
主要成分 雜質(zhì)，不大于
Ti B Al Si Sn Cr Fe Cu Zr Mo Fe Si C N H O 其他元素
單一 總和
TAD 碘法鈦 余量 — — — — — — — — — 0.03 — 0.03 0.01 0.015 0.05 — —
TA8 Ti-5Al-2.5Sn-3Cu-1.5Zr 余量 — 4.5～5.5 — 2.0～3.0 — — 2.5～3.2 1.0～1.5 — 0.30 0.15 0.10 0.06 0.015 0.15 0.10 0.40
TB1 Ti-3Al-8Mo-11Cr 余量 — 3.0～4.0 — — 10.0～11.5 — — — 7.0～8.0 0.30 0.15 0.10 0.05 0.012 0.15 0.10 0.40
TC5 Ti-Al-2.5Cr 余量 — 4.0～6.2 — — 2.0～3.0 — — — — 0.30 0.40 0.10 0.05 0.015 0.15 0.10 0.40
TC7 Ti-6Al-0.6Cr-0.4Fe-0.4Si-0.01B 余量 0.01 5.0～6.5 0.25～0.60 — 0.4～0.9 0.25～0.60 — — — — — 0.10 0.05 0.015 0.18 0.10 0.40
注：TB1、TC5為GB/T 3620.1—1983年制定國(guó)標(biāo)時(shí)刪除的牌號(hào)，TAB、TC7為GB/T 3620.1—1994年國(guó)標(biāo)修訂時(shí)刪除的牌號(hào)，TAD為GB/T 3620.1—2007修訂時(shí)刪除的牌號(hào)。
附 錄B
(資料性附錄)
本標(biāo)準(zhǔn)表2中工業(yè)純鈦與ASTM標(biāo)準(zhǔn)體系純鈦牌號(hào)對(duì)應(yīng)關(guān)系
本標(biāo)準(zhǔn)表2中工業(yè)純鈦與ASTM標(biāo)準(zhǔn)體系純鈦牌號(hào)對(duì)應(yīng)關(guān)系見表B.1。
表B.1 本標(biāo)準(zhǔn)表2中工業(yè)純鈦與ASTM標(biāo)準(zhǔn)體系純鈦牌號(hào)對(duì)應(yīng)關(guān)系
本標(biāo)準(zhǔn) ASTM標(biāo)準(zhǔn)
TA1G Grade 1(UNS Number R50250)
TA2G Grade 2(UNS Number R50400)
TA3G Grade 3(UNS Number R50550)
TA4G Grade 4(UNS Number R50700)
附 錄C
(規(guī)范性附錄)
鈦及鈦合金牌號(hào)命名規(guī)則
C.1牌號(hào)命名的基本規(guī)則
C.1.1 分類
C.1.1.1鈦及鈦合金牌號(hào)分為三類，即α、α-β和β。
C.1.1.2鈦及鈦合金牌號(hào)依據(jù)其名義成分含量計(jì)算所得的鉬當(dāng)量的結(jié)果進(jìn)行分類。
C.1.2命名規(guī)則
C.1.2.1鈦及鈦合金牌號(hào)的命名采用注冊(cè)制，牌號(hào)命名前應(yīng)進(jìn)行牌號(hào)注冊(cè)，統(tǒng)一命名。
C.1.2.2采用字母和數(shù)字表示鈦及鈦合金的牌號(hào)。
C.2牌號(hào)編制方法
C.2.1 牌號(hào)的第一位用大寫字母“T”表示鈦及鈦合金。
C.2.2牌號(hào)的第二位表示合金的類型，分別用大寫字母A、B和C表示，A表示工業(yè)純鈦、α型和近α型合金，B表示β型及近β型合金，C表示α-β型合金。
C.2.3牌號(hào)中的阿拉伯?dāng)?shù)字按注冊(cè)的先后自然順序排序。
C.2.4相同牌號(hào)的超低間隙合金在數(shù)字后加大寫字母“ELI”，數(shù)字與“ELI”之間無(wú)間隔。
C.3名義成分編制規(guī)則
C.3.1鈦合金牌號(hào)的名義成分僅列出必須控制范圍的元素。
C.3.2名義成分中元素含量的確定應(yīng)以其控制范圍的算術(shù)平均值為基本原則。
附 錄 D
(資料性附錄)
關(guān)于本標(biāo)準(zhǔn)與相關(guān)標(biāo)準(zhǔn)執(zhí)行問(wèn)題的說(shuō)明
D.1 TA0、TA1、TA2及TA3牌號(hào)的執(zhí)行說(shuō)明
本標(biāo)準(zhǔn)表1中規(guī)定的TA0、TA1、TA2及TA3分別對(duì)應(yīng)于2007年1月1日前發(fā)布的相關(guān)鈦國(guó)家標(biāo)準(zhǔn)、國(guó)家軍用標(biāo)準(zhǔn)、行業(yè)標(biāo)準(zhǔn)中相應(yīng)的TA0、TA1、TA2及TA3牌號(hào)和化學(xué)成分。
D.2 TA1GELI、TA1G、TA1G-1、TA2GELI、TA2G、TA3GELI、TA3G、TA4GELI、TA4G牌號(hào)的執(zhí)行說(shuō)明
本標(biāo)準(zhǔn)表1中規(guī)定的TA1GELI、TA1G、TA1G-1、TA2GELI、TA2G、TA3GELI、TA3G、TA4GELI、TA4G分別對(duì)應(yīng)于GB/T 2965—2007、GB/T 3621—2007、GB/T 3622—2012、GB/T 3623—2007、GB/T 3624—2010、GB/T 3625—2007、GB/T 12769—2007、GB/T 13810—2007、GB/T 14845—2007、GB/T 16598—2013、GB/T 26057—2010、GB/T 26058—2010、GB/T 26059—2010、GB/T 26723—2011、GJB 2218A—2008、GJB 2505A—2008、YS/T 658—2007、YS/T 750—2011、YS/T 794—2012、YS/T 795—2012、YS/T 885—2013標(biāo)準(zhǔn)中相應(yīng)的TA1ELI、TA1、TA1-1、TA2ELI、TA2、TA3ELI、TA3、TA4ELI及TA4牌號(hào)和化學(xué)成分。
D.3參考標(biāo)準(zhǔn)
GB/T 2965—2007 鈦及鈦合金棒材
GB/T 3621—2007 鈦及鈦合金板材
GB/T 3622—2012 鈦及鈦合金帶、箔材
GB/T 3623—2007 鈦及鈦合金絲
GB/T 3624—2010 鈦及鈦合金無(wú)縫管
GB/T 3625—2007 換熱器及冷凝器用鈦及鈦合金管
GB/T 12769—2007 鈦銅復(fù)合棒
GB/T 13810—2007 外科植入物用鈦及鈦合金加工材
GB/T 14845—2007 板式換熱器用鈦板
GB/T 16598—2013 鈦及鈦合金餅和環(huán)
GB/T 26057—2010 鈦及鈦合金焊接管
GB/T 26058—2010 鈦及鈦合金擠壓管
GB/T 26059—2010鈦及鈦合金網(wǎng)板
GB/T 26723—2011冷軋鈦帶卷
GJB 2218A—2008航空用鈦及鈦合金棒材和鍛坯
GJB 2505A—2008航空用鈦及鈦合金板材和帶材規(guī)范
YS/T 658—2007 焊管用鈦帶
YS/T 750—2011 熱軋鈦帶卷
YS/T 794—2012鈦種板
YS/T 795—2012高爾夫球頭用鈦及鈦合金板材
YS/T 885—2013鈦及鈦合金鍛造板坯