標準編號:	GB/T 22374-2018
中文名稱:	地坪涂裝材料
英文名稱:	Floor coating
中標分類:	Q18    裝修材料
行業分類:	GB    國家標準
發布機構:	國家市場監督管理總局 國家標準化管理委員會
發布日期:	2018-06-07
實施日期:	2019-5-1
標準狀態:	valid
替代舊標準:	GB/T 22374-2008 地坪涂裝材料
翻譯語言:	英文
文件格式:	PDF
中文字符數:	25000 字
翻譯價格(元):	1750.0
交付時間:	付款后 1 個工作日

Codeofchina.com is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative. This standard is developed in accordance with the rules given in GB/T 1.1-2009. This standard replaces GB/T 22374-2008 Floor coatings. In addition to a number of editorial changes, the following technical changes have been made with respect to GB/T 22374-2008 (the previous edition): ——the terms and definitions are modified (see Clause 3; Clause 3 in Edition 2008); ——the product classification is modified (see 4.1; 4.1 in Edition 2008); ——the items “total content of glycol ether and ether ester, total content of phthalic acid esters, free 4,4'-diaminodiphenylmethane (MDA), total volatile organic compound (TVOC) emission and formaldehyde emission" are added (see Table 1; Table 2 in Edition 2008); ——the item "stretching adhesive strength" is added in and “adhesion” is deleted from priming coat (see Table 2; Table 3 in Edition 2008); ——the technical requirements for floating coat of floor coatings are added (see Table 3); ——in top coat basic performance “stretching adhesive strength” is added for waterborne and solvent-borne floor coatings, “artificial weather resistance” for outdoor floor coating, “initial fluidity” for self-leveling floor coating, and “adhesion” is deleted from it (see Table 4; Table 4 in Edition 2008); ——the technical requirements for top coating of polymer cement floor coating are added (see Table 5); ——in top coat special performance items “elasticity”, “coating resistance to temperature change”, “scratch resistance” and “hot tire indentation resistance” are added, and “fluidity”, “stretching adhesive strength” and “artificial weather resistance” are deleted (see Table 6; Table 5 in Edition 2008); ——the test methods for volatile organic compound (VOC) content and free formaldehyde are modified (see 6.2.3, 6.2.4; 6.3.1 and 6.3.2 in Edition 2008); ——the test substrate is changed from asbestos cement sheet into non-asbestos fiber cement flat sheet (see 6.3.1.1.1; 6.2.1.1 in Edition 2008). ——the normative Annex B is added (see Annex B) and the normative Annex A is modified (see Annex A; Annex A in Edition 2008). This standard was proposed by China Building Materials Federation. This standard is under the jurisdiction of SAC/TC 195 National Technical Committee on Constructional Materials and Decorative Materials of Standardization Administration of China. The previous edition of standard replaced by this standard is as follows: ——GB/T 22374-2008. Floor coatings 1 Scope This standard specifies terms and definitions, classification and mark, requirements, test methods, inspection rules, marking, packaging, transport and storage of floor coatings. This standard is applicable to synthetic resin-based and polymer cement floor coating applied to cement mortar, concrete and other base surfaces for decoration, protection and special functions like anti-static, anti-slip, etc. of the ground. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. GB/T 250 Textiles - Tests for color fastness - Grey scale for assessing change in color GB/T 1633-2000 Plastics - Thermoplastic materials - Determination of vicat sofening temperature (VST) GB/T 1728-1979 Methods of test for drying time of coatings of paints and putties GB/T 1731 Determination of flexibility of films GB/T 1766 Paints and varnishes - Rating schemes of degradation of coats GB/T 1768 Paints and varnishes - Determination of resistance to abrasion - Rotating abrasive rubber wheel method GB/T 1865-2009 Paints and varnishes - Artificial weathering and exposure to artificial radiation - Exposure to filtered xenon-arc radiation GB/T 2411-2008 Plastics and ebonite - determination of indentation hardness by means of a duronmeter (Shore Hardness) GB/T 2567-2008 Test methods for properties of resin casting body GB/T 4100-2015 Ceramic tile GB/T 6682 Water for analytical laboratory use - Specification and test methods GIVT 6739 Paints and varnishes - Determination of film hardness by pencil test GB/T 8170 Rules of rounding off for numerical values & expression and judgement of limiting values GB 8624 Classification for burning behavior of building materials and products GB/T 9271 Paints and varnishes - standard panels for testing GB/T 9274-1988 Paints and varnishes - Determination of resistance to liquids GB 9743 Passenger car tyres GB/T 9754 Paints and varnishes - Determination of specular gloss of non-metallic paint films at 20°, 60°and 85° GB/T 9779-2015 Multi-layer coatings for architecture GB/T 9780-2013 Test method for dirt pickup resistance and stain removal of film of architectural coatings and paint GB/T 11186.2-1989 Methods for measuring the colour of paint films - Part 2: Colour measurement GB 11614 Plate glass GB/T 13491 General rule for packing of coatings GB/T 17671 Method of testing cements - Determination of strength (ISO Method) GIVT 18446 Binders for paints and varnishes - determination of monomeric diisocyanates in isocyanate resins GB 18581-2009 Indoor decorating and refurbishing materials - Limit of harmful substances of solvent based coatings for woodenware GB 18582-2008 Indoor decorating and refurbishing materials - Limit of harmful substances of interior architectural coatings GB 18583-2008 Indoor decorating and refurbishing materials - Limit of harmful substances of adhesives GB/T 23985-2009 Paints and varnishes - Determination of volatile organic compound (VOC) content - Difference method GB/T 23993 Determination of formaldehyde content of waterborne coatings - Spectrophtometric method with acetylacetone GB 24408-2009 Limit of harmful substances of exterior wall coatings GB 24613 Limit of harmful substances of coatings for toys JC/T 412.1-2006 Fiber cement flat sheets - Part 1: Non-asbestos fiber cement flat sheets JC/T 547 Adhesives for ceramic tiles JC/T 985-2017 Cementitious self-leveling floor mortar JC/T 2327-2015 Waterborne polyurethane screed material JG/T 25 Test method for temperature change resistance of architectural coatings JG/T 481-2015 Water-based interior wall coating with low-emission volatile organic compounds (VOC) SJ/T 11294 General specification of floor coating for electrostatic protection YB/T 4086-2017 Steel wool fiber 3 Terms and definitions For the purpose of this document, the terms and definitions given in GB 18582-2008 and JG/T 481-2015 and the following apply. 3.1 volatile organic compound (VOC) all organic compounds of which the initial boiling point is lower than or equal to 250℃ under the standard atmosphere pressure 101.3kPa [GB 18582-2008, Definition 3.1] 3.2 total volatile organic compound (TVOC) total collection of volatile organic compounds with retention time between n-hexane and n-hexadecane when analyzed with a non-polar column (with a polarity index less than 10) [JC/T 481-2015, Definition 3.2] 3.3 waterborne floor coaling synthetic resin-based floor coating with water as the main dispersion medium 3.4 solvent-borne floor coating floor coating with volatile organic compounds, which will not become component of the coating after solidification, as dispersion medium 3.5 solvent-free floor coating floor coating with organic compounds, which will exist as film-forming substance after solidification, as dispersion medium 3.6 polymer cement floor coating floor coating formulated by adopting water-based polymer and cement-based cementitious materials, into which fillers, aggregates and other additives are added 3.7 organic crosslinking reaction polymer cement floor coating floor coating formulated by adopting multi-component reactive polymer (polyurethane) and cement-based cementitious materials, into which fillers, aggregates and other additives are added 3.8 non-organic crosslinking reaction polymer cement floor coating floor coating formulated by adopting single-component polymer (powder or emulsion) and cement-based cementitious materials, into which fillers, aggregates and other additives are added 3.9 floor coating system multi-layer flooring system with functional and decorative effects, which consists of priming coat, floating coat (optional) and top coat 3.10 light load floor coating used for ground on which passengers and non-motor vehicles and, occasionally, motor vehicles with rubber tires pass through 3.11 heavy load floor coating used for ground on which forklifts and those with hard plastic tires pass through and there is occasionally impact load 4 Classification and mark 4.1 Classification Floor coating is classified according to the following four ways: a) Floor coatings are classified according to their dispersion media into waterborne floor coaling (S), solvent-free floor coating (W), solvent-borne floor coating (R) and polymer cement floor coating (J). According to the film formation mechanism, the polymer cement floor coating is further classified into organic crosslinking reaction polymer cement floor coating and non-organic crosslinking reaction polymer cement floor coating (FJ). b) Floor coating is classified according to the coating structure into priming coat (D), floating coat (Z) and top coat (M). c) Floor coating is classified according to use place into indoor (SN) and outdoor (SW) coatings. d) Floor coating is classified according to traffic carrying capacity into light load (QZ) and heavy load (ZZ). 4.2 Mark The products are marked in the sequence of product name, standard number, dispersion medium, coating structure, use place and traffic carrying capacity. Example: Top coat of solvent-borne floor coating used for outdoor light load floor is marked as: floor coating GB/T 22374-20 ×× R M SW QZ

Foreword i 1 Scope 2 Normative references 3 Terms and definitions 4 Classification and mark 4.1 Classification 4.2 Mark 5 Requirements 5.1 Requirements for limit of harmful substances 5.2 Physical property requirements 6 Test method 6.1 Test environment 6.2 Test on limit of harmful substances 6.3 Test methods for physical property 7 Inspection rules 7.1 Inspection classification 7.2 Batching 7.3 Sampling 7.4 Judgment rules 8 Marking, packaging, transport and storage 8.1 Marking 8.2 Packaging 8.3 Transport 8.4 Storage Annex A (Normative) Determination of free 4.4'-diaminodiphenylmethane (MDA) Annex B (Normative) Determination of hot tire indentation resistance

地坪涂裝材料 1范圍 本標準規定了地坪涂裝材料的術語和定義、分類和標記、要求、試驗方法、檢驗規則、標志、包裝、運輸和貯存。 本標準適用于涂裝在水泥砂漿、混凝土等基面上，對地面起裝飾、保護作用以及具有特殊功能(防靜電性、防滑性等）要求的合成樹脂基和聚合物水泥復合地坪涂裝材料。 2規范性引用文件 下列文件對于本文件的應用是必不可少的。凡是注日期的引用文件，僅注日期的版本適用于本文件。凡是不注日期的引用文件，其最新版本(包括所存的修改單）適用于本文件。 GB/T 250紡織品 色牢度試驗 評定變色用灰色樣卡 GB/T 1633—2000 熱塑性塑料維卡軟化溫度(VST）的測定 GB/T 1728—1979 漆膜、膩子膜干燥時間測定法 GB/T 1731 漆膜柔韌性測定法 GB/T 1766 色漆和清漆 涂層老化的評級方法 GB/T 1768 色漆和清漆 耐磨性的測定 旋轉橡膠砂輪法 GB/T 1865—2009 色漆和清漆 人工氣候老化和人工輻射暴露 濾過的氙弧輻射 GB/T 2411—2008 塑料和硬橡膠 使用硬度計測定壓痕硬度(邵氏硬度） GB/T 2567—2008 樹脂澆鑄體性能試驗方法 GB/T 4100—2015 陶瓷磚 GB/T 6682 分析實驗室用水規格和試驗方法 GIVT 6739 色漆和清漆 鉛筆法測定漆膜硬度 GB/T 8170 數值修約規則與極限數值的表示和判定 GB 8624 建筑材料及制品燃燒性能分級 GB/T 9271 色漆和清漆 標準試板 GB/T 9274—1988 色漆和清漆 耐液體介質的測定 GB 9743 轎車輪胎 GB/T 9754 色漆和清漆 不含金屬顏料的色漆漆膜的20°、60°和85°鏡面光澤的測定 GB/T 9779—2015 復層建筑涂料 GB/T 9780—2013 建筑涂料涂層耐沾污性試驗方法 GB/T 11186.2-1989 漆膜顏色的測量方法 第二部分：顏色測量 GB 11614 平板玻璃 GB/T 13491 涂料產品包裝通則 GB/T 17671 水泥膠砂強度檢驗方法(ISO法） GIVT 18446 色漆和清漆用漆基 異氰酸酯樹脂中二異氰酸酯單體的測定 GB 18581—2009 室內裝飾裝修材料 溶劑型木器涂料中有害物質限量 GB 18582—2008 室內裝飾裝修材料 內墻涂料中有害物質限量 GB 18583—2008 室內裝飾裝修材料 膠粘劑中有害物質限量 GB/T 23985—2009 色漆和清漆 揮發性有機化合物(VOC）含量的測定 差值法 GB/T 23993 水性涂料中甲醛含量的測定 乙酰丙酮分光光度法 GB 24408—2009 建筑用外墻涂料中有害物質限量 GB 24613 玩具用涂料中有害物質限量 JC/T 412.1—2006 纖維水泥平板 第1部分：無石棉纖維水泥平板 JC/T 547陶瓷磚膠粘劑 JC/T 985—2017 地面用水泥基自流平砂漿 JC/T 2327—2015 水性聚氨酯地坪 JG/T 25 建筑涂料涂層耐溫變性試驗方法 JG/T 481—2015 低揮發性有機化合物(VOC）水性內墻涂覆材料 SJ/T 11294 防靜電地坪涂料通用規范 YB/T 4086—2017 鋼棉纖維 3術語和定義 GB 18582—2008、JG/T 481—2015界定的以及下列術語和定義適用于本文件。 3.1 揮發性有機化合物(VOC） volatile organic compound 在101.3 kPa標準大氣壓下，任何初沸點低于或等于250℃的有機化合物。 [GB 18582—2008,定義 3.1] 3.2 總揮發性有機化合物(TVOC） total volatile organic compound 用非極性色譜柱(極性指數小于10）對采集樣品進行分析，保留時間在正己烷和正十六烷之間的揮發性有機化合物總和。 [JG/T 481—2015,定義 3.2] 3.3 水性地坪涂裝材料 waterborne floor coaling 以水為主要分散介質的合成樹脂基地面涂裝類材料。 3.4 溶劑型地坪涂裝材料 sol vent-borne floor coating 以具有揮發性的且固化后不能成為涂層組份的有機物為分散介質的地面涂裝類材料。 3.5 無溶劑型地坪涂裝材料 solvent-free floor coating 以有機物為分散介質且固化后作為成膜物質存在的地面涂裝類材料。 3.6 聚合物水泥復合地坪涂裝材料 polymer cement floor coating 由水性聚合物和水泥基膠凝材料為主要原料，加入填料、骨料及其他助劑配制而成的地面涂裝類材料。 3.7 有機交聯反應型聚合物水泥復合地坪涂裝材料 organic crosslinking reaction polymer cement floor coating 由多組分反應型聚合物(聚氨酯）和水泥基膠凝材料為主要原料，加入填料、骨料及其他助劑配制而成的地面涂裝類材料。 3.8 非有機交聯反應型聚合物水泥復合地坪涂裝材料 non-organic crosslinking reaction polymer cement floor coating 由單組份聚合物(膠粉或乳液）和水泥基膠凝材料為主要原料，加入填料、骨料及其他助劑配制而成的地面涂裝類材料。 3.9 地坪涂裝材料涂層體系 floor coating system 由底涂、中涂(可選）和面涂組成的具有功能性和裝飾效果的多層地坪體系。 3.10 輕載地坪light load floor 用于人行交通及非機動車，偶爾有橡膠輪胎的機動車通行的地面涂裝類材料。 3.11 重載地坪 heavy load floor 用于叉車及有硬塑輪胎的叉車通行，偶爾有沖擊荷載的地面涂裝類材料。 4分類和標記 4.1分類 地坪涂裝材料按下列4種方式分類： a） 地坪涂裝材料按其分散介質分為水性地坪涂裝材料(S）、尤溶劑型地坪涂裝材料(W）、溶劑型地坪涂裝材料(R）;聚合物水泥復合型地坪涂裝材料(J）。根據成膜機理，將聚合物水泥復合型地坪涂裝材料又分為：有機交聯反應型聚合物水泥復合地坪涂裝材料(JJ）和非有機交聯反聚合物水泥復合地坪涂裝材料(FJ）。 b） 地坪涂裝材料按涂層結構分為：底涂(D）、中涂(Z）、面涂(M）。 c）地坪涂裝材料按使用場所分為：室內(SN）和室外(SW）。 d）地坪涂裝材料按交通承載量分為：輕載(QZ）、重載(ZZ）。 4.2標記 按產品名稱、標準號、分散介質、涂層結構、使用場所、交通承載量的順序標記示例： 溶劑型室外輕載地坪涂裝材料面涂標記為：地坪涂裝材料GB/T 22374—20×× R M SW QZ 5要求 5.1有害物質限量要求 地坪涂裝材料有害物質限量應符合表1的要求。 表1地坪涂裝材料有害物質限量的要求 序號 項目 指標 S型 R型 W型 J型 1 揮發性有機化合物含量(VOC）/(g/L）≤ 120 500 60 50 2 游離中醛/(mg/kg） ≤ 100 500 100 100 3 苯(g/kg） ≤ — 1 0.1 — 4 甲笨、乙苯、二甲苯的總和(g/kg） ≤ — 200 10 — 5 苯、甲苯、乙苯、二甲苯的總和/(g/kg） ≤ 5 — — 5 6 游離二異氰酸酯(TDI、HDI）a(限聚氨酯類）(g/kg）≤ 2 — 7 乙二醇醚及醚酯總和/(mg/kg） ≤ 300 8 鄰苯二甲酸酯含量/% ≤ 鄰苯二甲酸二異辛酯 (DEHP）、鄰苯二甲酸二丁酯 (DBP）和鄰苯二甲酸丁芐酯 (BBP）總和 — 0.1 — 鄰苯二甲酸二異壬酯 (DINP）、鄰苯二甲酸二異 酯(DIDP）和鄰苯二甲酸二辛酯(DNOP）總和 — 0.1 — 9 游離4,4’-二氨基二苯中烷(MDA）b(限環氧類）/(g/kg） ≤ 10 — 10 可溶性重金屬c/(mg/kg） ≤ 鉛(Pb） 30 鎘(Cd） 30 鉻(Cr） 30 汞(Hg） 10 11 總揮發性有機化合物(TVOC）釋放量b/(mg/m3） ≤ 10 商定 20 10 12 甲醛釋放量b/(mg/m3） ≤ 0.1 a 單組分水性地坪涂裝材料不測。 b 僅適用于室內地坪涂裝材料 c 僅適用于有色地坪涂裝材料。 5.2物理性能要求 5.2.1地坪涂裝材料底涂 地坪涂裝材料底涂應符合表2的要求。 表2地坪涂裝材料底涂的要求 序號 項目 指標 S型 R型 W型 1 容器中狀態 攪拌混合后均勻，無硬塊 2 干燥時間/h 表干 ≤ 8 4 6 實干 ≤ 48 24 3 耐堿性(飽和Ca(OH）2，48 h） 漆膜完整，不起泡，不剝落，允許輕微變色 4 拉伸粘結強度/MPa ≥ 2.0 5.2.2地坪涂裝材料中涂 地坪涂裝材料中涂應符合表3的要求。 表3 地坪涂裝材料中涂的要求 序號 項目 指標 S型 R型 W型 1 容器中狀態 攪拌混合后均勻，無硬塊 2 干燥時間/h 表干 ≤ 8 4 6 實干 ≤ 48 24 3 耐堿性(飽和Ca(OH）2,48h） 漆膜完整，不起泡，不剝落，允許輕微變色 4 抗壓強度/MPa ≥ —— 45 5.2.3 地坪涂裝材料面涂及涂層體系 5.2.3.1基本性能 水性、溶劑型、無溶劑型地坪涂裝材料面涂的基本性能應符合表4的要求，涂層體系的基本性能應符合表4中第8項?第13項的要求。聚合物水泥復合地坪涂裝材料面涂的基本性能應符合表5的要求。 表4水性、溶劑型、無溶劑型地坪涂裝材料面涂及涂層體系的基本性能要求 序號 項目 指標 S型 R型 V型 1 容器中狀態 攪拌后呈均勻狀態，無硬塊 2 涂膜外觀 表面平整、無明顯可見的縮孔、浮色、發花、起皺、針孔、開裂等現象 3 干燥時間/h 表干 ≤ 8 實干 ≤ 48 4 初始流動度a/mm ≥ 140 表4 (續） 序號 項目 指標 S型 R型 W型 5 硬度 鉛筆硬度(擦傷） 商定 — 邵氏硬度(D型） — 商定 6 耐磨性(750 g/500 r）/g ≤ 0.050 0.030 7 抗壓強度/MPa ≥ — 45 8 拉伸粘結強度/MPa 標準條件 ≥ 2.0 浸水后 ≥ 2.0 9 耐沖擊性 輕載(500 g鋼球） 涂膜無裂紋、無剝落 重載(1000 g鋼球） 10 防滑性(干摩擦系數） ≥ 0.50 11 耐水性(168 h） 不起泡，不剝落，允許輕微變色，2 h后恢復 12 耐化學性 耐堿性(20%NaOH，72 h） 不起泡，不剝落，允許輕微變色 耐酸性(10%H2SO4,48 h） 不起泡，不剝落，允許輕微變色 耐油性(120#溶劑油，72 h） 不起泡，不剝落，允許輕微變色 13 耐人工氣候老化性b 時間商定(不低于400 h）， 不起泡、不剝落、無裂紋，粉化≤1級，變色≤2級 a僅適用于自流平地坪涂裝材料。 b僅適用于室外用地坪涂裝材料。 表5聚合物水泥復合地坪涂裝材料面涂的基本性能要求 序號 項目 指標 JJ型 FJ型 1 容器中狀態 液體組分攪拌后呈均勻狀態；粉體組分應無結塊 2 涂膜外觀 表曲無裂紋，顏色均勻 3 可操作時間/ min 商定 — 4 尺寸變化率/% — -0.15 ?+0.15 5 初始流動度a /mm ≥ 130 6 維卡軟化點b/℃ ≥ 140 — 7 抗壓強度/MPa ≥ 24 h 20.0 6.0 7 d 40.0 — 28 d — 30.0 8 抗折強度/MPa ≥ 24 h 5.0 2.0 7 d 10.0 — 28 d — 7.0 表5 (續） 序號 項目 指標 JJ型 FJ型 9 耐磨性(500 g/100 r）/g ≤ 0.15 0.50 10 防滑性(干摩擦系數） ≥ 0.6 0.6 11 拉伸粘結強度/MPa ≥ 2.0 1.0 12 耐沖擊性(1 000 g鋼球） 表面無裂紋、無剝落 13 耐水性(168 h） 無起泡，無剝落，無裂紋， 無變色 無起泡，無剝落，無裂紋， 無變色 14 耐化學性 耐堿性 (20%NaOH,72 h） 無起泡，無剝落，無裂紋. 允許輕微變色 無起泡，無剝落，無裂紋， 允許輕微變色 耐酸性(10%H2SO4,48 h） 無起泡，無剝落，無裂紋， 允許輕微變色 — 耐油性(120#溶劑油，72 h） 無起泡，無剝落，無裂紋， 允許輕微變色 無起泡，無剝落，無裂紋， 允許輕微變色 15 耐鹽水性(3%NaCl，168 h） 無起泡，無剝落，無裂紋， 允許輕微變色 無起泡，無剝落，無裂紋， 允許輕微變色 a僅適用自流平聚合物水泥復合地坪涂裝材料。 b僅適用于溫度高的場所。 5.2.3.2 特殊性能 特殊場合使用的地坪涂裝材料面涂或涂層體系的性能除應符合表4、表5的要求外，還應符合表6 的要求。 表6地坪涂裝材料面涂或涂層體系特殊性能要求 序號 項目 指標 1 高防滑性a,b 濕摩擦系數 ≥ 0.70 2 防靜電性a,c 表面電阻(導靜電型）/Ω ≥5×104～＜1×106 體積電阻(導靜電型）/Ω 表面電阻(靜電耗散型）/Ω ≥1×106～＜1×109 體積電阻(靜電耗散型）/Ω 3 燃燒性能a,d 商定 4 耐特殊化學介質性a,e 商定 5 彈性f 拉伸強度/MPa ≥ 商定 斷裂伸長率/% ≥ 商定 柔韌性/mm 商定 ? 表6 (續） 序號 項目 指標 6 涂層耐溫變性a,g 漆膜表面無起泡、剝落、變色等現象 7 抗劃傷性h ≤ 商定 8 抗熱胎壓痕性a,i △E*≤3.0(單色）；變色≤1級(彩色） a 可根據有關方商定測試配套底涂后或與底涂和中涂后的性能。 b 適用于對防滑性有特殊要求的場所。 c 適用于需防靜電的場所。 D 適用于對燃燒性能有要求的場所。 e 適用于需接觸高濃度酸、堿、鹽等化學腐蝕性藥品的場所。 f 適用于彈性地坪涂裝材料。 g 適用于冷庫或蒸汽消毒，有溫度變化差異的使用場所。 h 適用于表面光滑地坪涂裝材料。 i 適用于車庫、停車場等場所。 6試驗方法 6.1試驗環境 標準試驗條件為溫度(23±2）°C，相對濕度(50 ± 5）%。試樣應在此條件下放置至少24 h后進行試驗。 6.2 有害物質限量試驗方法 6.2.1一般規定 按產品規定的配比混合后進行試驗。如稀釋劑的使用量為某一范圍時，應按照最大稀釋量稀釋后進行試驗。 6.2.2有害物質釋放量試板制備 6.2.2.1試驗基材 平板玻璃應符合GB 11614的規定。 6.2.2.2試板制備 有害物質釋放量試板應符合表7的規定。 表7有害物質釋放量試板制備 項目 試板類型 試件數量 塊 尺寸 mm 一次涂刷 g S型、R型 W型 J型 總揮發性有機化合(TVOC） 釋放量、甲醛釋放量 平板玻璃 2 200×300 12.0 ± 0.2 75 ± 2 120 ± 2 6.2.3 揮發性有機化合物含量(VOC) 水性地坪涂裝材料的揮發性有機化合物含量(VOC)按GB 18582-2008中附錄A規定進行試驗。 溶劑塑及無溶劑型地坪涂裝材料的揮發性有機化合物含量(VOC)按GB/T 23985規定進行試驗，并按GB/T 23985-2009中8.3式(2) 計算。將試樣攪拌均勻后，稱取(l.0±0.l)g試樣置于盤中，溶劑型地坪涂裝材料立即放入(105±2)℃高溫試驗箱中1h;無溶劑型地坪涂裝材料在(23±2)℃、相對濕度(50±5)%條件下放置24 h后放入(105±2)℃高溫試驗箱中1h。 聚合物水泥復合地坪涂裝材料按GB/T 23985規定進行試驗?并按GB/T 23985-2009中8.4式(3)計算。 6.2.4 游離甲醛 水性地坪涂裝材料的游離甲醛按GR/T 23993規定進行試驗，溶劑型、無溶劑型及聚合物水泥復合地坪涂裝材料的游離甲醛按GB 18583-2008中附錄A中溶劑型膠粘劑的規定進行試驗。 6.2.5苯及甲苯、乙苯、二甲苯的總和 水性地坪涂裝材料的苯及甲苯、乙苯、二甲苯總和按GB 18582-2008中附錄A進行試驗。水性地坪涂裝材料不稀釋。 溶劑型、無溶劑型和聚合物水泥復合地坪涂裝材料的苯及甲苯、乙苯、二甲苯的總和按GB 18581-2009中附錄B規定進行試驗。若產品規定了稀釋比例或產品由雙組分或多組分組時，應分別測定稀釋劑和各組分中的含量，再按產品規定的配比計算混合后地坪涂裝材料中的總量。如稀釋劑的使用量為某一范圍時，應按照推薦的最大稀釋量進行計算。固體組分不測含量，僅參與計算。 6.2.6游離二異氰酸酯(TDI，HDI) 按GB/T 18446規定進行試驗。若規定了稀釋比例或由雙組分或多組分組成時，應先測定固化劑(含有二異氰酸酯化合物）中的含量，再按產品規定的配比計算混合后地坪涂裝材料中的含量。如稀釋劑的使用量為某一范圍時，應按照推薦的最小稀釋量進行計算。固體組分不測含量，僅參與計算。 6.2.7 乙二醇醚及醚酯總和 乙二醇醚及醚酯總和為；乙二醇甲醚、乙二醇甲醚醋酸酯、乙二醇乙醚、乙二醇乙醚醋酸酯和二乙二醇丁醚醋酸酯、乙二醇丁醚、乙二醇丁醚醋酸酯的含量總和。 水性地坪涂裝材料的乙二醇醚及醚酯總和按GB 24408-2009中附錄A的方法進行試驗。水性地坪涂裝材料不稀釋。 溶劑型、無溶劑型和聚合物水泥復合地坪涂裝材料的乙二醇醚及醚酯總和按GB 24408-2009中附錄D的方法進行試驗。若產品規定了稀釋比例或產品由雙組分或多組分組成時.，應分別測定稀釋劑和各組分中的含量，再按產品規定的配比計算混合后地坪涂裝材料中的總量。如稀釋劑的使用量為某一范圍時，應按照推薦的最大稀釋量進行計算。固體組分不測含量，僅參與計算。 6.2.8 鄰苯二甲酸酯含量 按GB 24613規定進行。 6.2.9 游離4.4'-二氨基苯甲烷(MDA) 按附錄A規定進行試驗，以固化劑中的含量報出。 6.2.10 可溶性重金屬 按GB 18582-2008中附錄D規定進行。 6.2.11 總揮發性有機化合物(TVOC)釋放量、甲醛釋放量 按JG/T 481-2015中7.3規定進行。 6.3 物理性能試驗方法 6.3.1 試驗樣板制備 6.3.1.1試驗基材 6,3.1.1.1 無石棉纖維水泥平板應符合JC/T 412.1-2006中厚度為4mm?6 mm的NAF H V級板的規定。 6.3.1.1.2 馬口鐵板、鋼板、鋁板或玻璃板的材質要求及處理應符合GB/T 9271的規定。 6.3.1.1.3 混凝土板應符合JC/T 547的規定。 6.3.1.2 試樣制備 6.3.1.2.1 地坪涂裝材料制板的要求 將地坪涂裝材料各組份按產品說明書提供的使用比例混合，若給出一個值域范圍，則取中間值。 將試樣混合并攬拌均勻，以產品說明書提供的施工方法將試樣涂布于符合6.3.1.1規定的試驗基材表面，如沒有特別規定則采用空氣噴涂法或刷涂法制板。 需進行多道涂裝或涂層體系制備時按產品說明書進行。如沒有特別規定按表8、表9的要求進行制備和養護，涂裝間隔為24h。制備好的試板和試件的表面應平整、無裂紋。