Codeofchina.com is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative.
The product indices in Table 1 of this Standard are all compulsory and other content is recommendatory.
This standard is not equivalent to the corresponding Japanese Industrial Standard JIS K1475: 2006 Poly Aluminium Chloride for Water Supply(Japanese version) and American Water Works Association Standard ANSI/AWWA B 408: 2003 Liquid Poly Aluminium Chloride (English Version).
Compared with JIS K 1475: 2006 and ANSI/AWWA B 408: 2003, the main differences are as follows:
- liquid poly aluminium chloride and solid poly aluminium chloride are included in this Standard.
- the technology index of basicity is increased according to the technological advance of poly aluminium chloride, and the production process and material source of poly aluminium chloride industry in China.
- the inspection method related to the heavy metal indices is changed.
- “the determination of ammoniacal nitrogen” is deleted.
This Standard replaces GB 15982-2003 Water Treatment Chemical – Poly Aluminium Chloride. Compared with GB 15890-2003, the main differences are as follows:
- This Standard name was changed into Poly Aluminium Chloride for Treatment of Drinking Water
- The technical index in Table 1 has been changed.
- The inspection method of aluminum oxide with CuSO4 standard volumetric solution is added.
- The determination method of some technical indices is modified.
-"The determination of ammonia nitrogen" is deleted.
Appendix A is informative.
This standard was proposed by China Petroleum and Chemical Industry Association.
This standard is under the jurisdiction of Subcommittee on Water Treatment Agent of the National Technical Committee on Chemical of Standardization Administration of China (SAC/TC 63/SC5).
Drafting organizations: Shenzhen Zhognrun Water Industry Technology Development Co.,Ltd., Tongji University, Taichang Xinxing Light Industry Auxiliary Factory, Shenzhen Qingyuan Water Purifier Co., Ltd, Shandong Purifiers Chemical Co., Ltd, Kemira Water Treatment Technology, Dongguan Huaqing Water Purification Materials Co., Ltd, Jiaozuo Aierfuke Chemical Industry Co., Ltd., Henan Huaquan Water Supply Material Head Factory, Henan New Century Purification material Co.Ltd.
Participating drafting organization of this standard: Tianjin Chemical Research and Design Institute of CNOOC, Wuxi Bisheng Water Treatment Agent Co.Ltd, Wuhan Zhongquin Fine Chemicals Co., Ltd., Gongyi Zhitian Water Purifying Materials Co., Ltd, Gongyi Yuqing Water Purigying Materials Co., Ltd., Gongyi Fuyyuan Water Purification Materials Co., Ltd, Chongqing University and Ningbo Huaguang Water Purifying Agent Industrial Corporation.
Chief drafting staff of this standard: Li Runsheng, Li Fengting, Tao Futang, Zhang Minquan, Jia Jiushun, Zhou Peng, Wang Longqing, Xu Zhiyuan, Yuan Mengbin and Tie Guibo.
The previous editions of the standards replaced by this standard are as:
- GB 15892—1995 and GB 15892—2003.
Poly Aluminium Chloride for Treatment of Drinking Water
生活飲用水用聚氯化鋁
1 Scope
This Standard specifies the technical requirements, test methods, test rules, packing, marking, transportation and storage of poly aluminium chloride for treatment of drinking water.
This Standard is applicable to poly aluminium chloride for treatment of drinking water. This product is mainly used in treatment of drinking water. Industrial synthetic hydrochloric acid shall be adopted for the raw material hydrochloric acid to produce poly aluminium chloride; the industrial alumina-hydroxide, kaolin, boehmite, gibbsite and calcium aluminate for water treatment agent shall be adopted for aluminiferous raw materials.
Rational formula Aln(OH)mCl(3n-m) 0
Contents
Foreword I
1 Scope
2 Normative References
3 Product Classification
4 Requirements
5 Test Methods
6 Test Rules
7 Marking, Packing, Transportation and Storage
Appendix A (Informative) Judgment of Coagulation Performance
生活飲用水用聚氯化鋁
1 范圍
本標(biāo)準(zhǔn)規(guī)定了生活飲用水用聚氯化鋁的要求、試驗(yàn)方法、檢驗(yàn)規(guī)則、包裝、標(biāo)志、運(yùn)輸和貯存。
本標(biāo)準(zhǔn)適用于生活飲用水用聚氯化鋁。該產(chǎn)品主要用于生活飲用水的凈化。生產(chǎn)聚氯化鋁的原料鹽酸,應(yīng)采用工業(yè)合成鹽酸;含鋁原料,應(yīng)采用工業(yè)氫氧化鋁、高嶺土、一水軟鋁石、三水鋁石和水處理劑用鋁酸鈣。
示性式:Aln(OH)mCl(3n-m) 0<m<3n
2 規(guī)范性引用文件
下列文件中的條款通過(guò)本標(biāo)準(zhǔn)的引用而成為本標(biāo)準(zhǔn)的條款。凡是注日期的引用文件,其隨后所有的修改單(不包括勘誤的內(nèi)容)或修訂版均不適用于本標(biāo)準(zhǔn),然而,鼓勵(lì)根據(jù)本標(biāo)準(zhǔn)達(dá)成協(xié)議的各方研究是否可使用這些文件的最新版本。凡是不注日期的引用文件,其最新版本適用于本標(biāo)準(zhǔn)。
GB/T 191 包裝儲(chǔ)運(yùn)圖示標(biāo)志
GB/T 601 化學(xué)試劑 標(biāo)準(zhǔn)滴定溶液的制備
GB/T 602 化學(xué)試劑 雜質(zhì)測(cè)定用標(biāo)準(zhǔn)溶液的制備(GB/T 602—2002,ISO 6353-1:1982,NEQ)
GB/T 603 化學(xué)試劑 試驗(yàn)方法中所用制劑及制品的制備(GB/T 603—2002,ISO 6353-1:1982,NEQ)
GB/T 610 化學(xué)試劑 砷測(cè)定通用方法(GB/T 610—2008,ISO 6353-1:1982,NEQ)
GB/T 6678 化工產(chǎn)品采樣總則
GB/T 6682 分析實(shí)驗(yàn)室用水規(guī)格和試驗(yàn)方法(GB/T 6682—2008,ISO 3696:1987,MOD)
GB/T 8946 塑料編織袋
3 產(chǎn)品分類(lèi)
聚氯化鋁按型態(tài)分為液體和固體兩類(lèi)。
4 要求
4.1 外觀(guān)
液體:無(wú)色至黃褐色液體。
固體:白色至黃褐色顆粒或粉末。
4.2 生活飲用水用聚氯化鋁指標(biāo)應(yīng)符合表1要求。
表 1
指標(biāo)名稱(chēng) 指 標(biāo)
液體 固體
氧化鋁(Al2O3)的質(zhì)量分?jǐn)?shù)/% ≥ 10.0 29.0
鹽基度/% 40.0~90.0
密度(20℃)/(g/cm3) ≥ 1.12 —
不溶物的質(zhì)量分?jǐn)?shù)/% ≤ 0.2 0.6
pH值(10g/L水溶液) 3.5~5.0
砷(As)的質(zhì)量分?jǐn)?shù)/% ≤ 0.0002
鉛(Pb)的質(zhì)量分?jǐn)?shù)/% ≤ 0.001
鎘(Cd)的質(zhì)量分?jǐn)?shù)/% ≤ 0.0002
汞(Hg)的質(zhì)量分?jǐn)?shù)/% ≤ 0.00001
六價(jià)鉻(Cr+6)的質(zhì)量分?jǐn)?shù)/% ≤ 0.0005
注:表中液體產(chǎn)品所列As、Pb、Cd、Hg、Cr+6、不溶物指標(biāo)均按Al2O310%計(jì)算,Al2O3含量≥10%時(shí),應(yīng)按實(shí)際含量折算成Al2O310%產(chǎn)品比例計(jì)算各項(xiàng)雜質(zhì)指標(biāo)。
5 試驗(yàn)方法
本標(biāo)準(zhǔn)所用試劑,除非另有規(guī)定,應(yīng)使用分析純?cè)噭┖头螱B/T 6682中三級(jí)水的規(guī)定。
試驗(yàn)中所需標(biāo)準(zhǔn)滴定溶液、雜質(zhì)標(biāo)準(zhǔn)溶液、制劑及制品,在沒(méi)有注明其他要求時(shí),均按GB/T 601、GB/T 602、GB/T 603的規(guī)定制備。
安全提示:本標(biāo)準(zhǔn)使用的強(qiáng)酸、強(qiáng)堿具有腐蝕性,使用時(shí)應(yīng)注意。濺到身上時(shí),用大量水沖洗。
5.1 氧化鋁(Al2O3)含量的測(cè)定(仲裁法)
5.1.1 氯化鋅標(biāo)準(zhǔn)溶液滴定法
5.1.1.1 方法提要
用硝酸將試樣解聚,在pH=3時(shí)加過(guò)量的乙二胺四乙酸二鈉溶液使EDTA與鋁離子絡(luò)合,然后用氯化鋅標(biāo)準(zhǔn)滴定溶液回滴過(guò)量EDTA溶液。
5.1.1.2 試劑和材料
5.1.1.2.1 硝酸溶液:1+12。
5.1.1.2.2 氨水溶液:1+1。
5.1.1.2.3 乙二胺四乙酸二鈉(EDTA)溶液:c(EDTA)約為0.05mol/L。
5.1.1.2.4 乙酸-乙酸鈉緩沖溶液(pH=5.5):稱(chēng)取乙酸鈉(三水)272g溶于水中,加冰乙酸19mL,稀釋至1000mL。
5.1.1.2.5 氧化鋁標(biāo)準(zhǔn)溶液:1mL含0.001g Al2O3。
稱(chēng)取0.5293g高純鋁(≥99.99%),精確至0.2mg,置于200mL聚乙烯杯中,加水20mL,加氫氧化鈉約3g,使其全部溶解透明(必要時(shí)在水浴上加熱),用鹽酸溶液(1+1)調(diào)節(jié)至酸性后再加10mL,使其透明,冷卻,移入1000mL容量瓶,稀至刻度,搖勻。
5.1.1.2.6 百里酚藍(lán)溶液:1g/L乙醇溶液。
5.1.1.2.7 二甲酚橙指示液:5g/L。
5.1.1.2.8 氯化鋅標(biāo)準(zhǔn)滴定溶液:c(ZnCl2)約0.025mol/L。
5.1.1.2.8.1 配制
稱(chēng)取3.5g氯化鋅(ZnCl2),溶于鹽酸溶液[0.05%(體積分?jǐn)?shù))]中,稀釋至1L,搖勻。
5.1.1.2.8.2 標(biāo)定
移取20.00mL EDTA溶液,置于250mL錐形瓶中,以下按5.1.1.3步驟進(jìn)行操作,讀出氯化鋅標(biāo)準(zhǔn)滴定溶液的消耗量V0,mL。
移取20.00mL EDTA溶液和40mL氧化鋁標(biāo)準(zhǔn)溶液,置于250mL錐形瓶中,以下按5.1.1.3步
驟進(jìn)行操作,讀出氯化鋅標(biāo)準(zhǔn)滴定溶液的消耗量V,mL。
5.1.1.2.8.3 結(jié)果計(jì)算
氯化鋅標(biāo)準(zhǔn)滴定溶液濃度c(ZnCl2),數(shù)值以摩爾每升(mol/L)表示,按式(1)計(jì)算:
c(ZnCl2)= ………………………………(1)
式中:
V1——氧化鋁標(biāo)準(zhǔn)溶液的體積的數(shù)值,單位為毫升(mL);
c1——氧化鋁標(biāo)準(zhǔn)溶液的濃度的數(shù)值,單位為克每毫升(g/mL);
M——氧化鋁的摩爾質(zhì)量的數(shù)值,單位為克每摩爾(g/mol)(M=101.96);
V0——空白消耗氯化鋅標(biāo)準(zhǔn)滴定溶液的體積的數(shù)值,單位為毫升(mL);
V——返滴定時(shí)消耗氯化鋅標(biāo)準(zhǔn)滴定溶液的體積的數(shù)值,單位為毫升(mL)。
5.1.1.3 分析步驟
稱(chēng)取約8g液體試樣或2.5g固體試樣,精確至0.2mg。用不含二氧化碳的水溶解,移入250mL容量瓶中,稀釋至刻度,搖勻。若稀釋液渾濁,用中速濾紙干過(guò)濾,此為試液A。
用移液管移取10mL試液A,置于250mL錐形瓶中,加10mL硝酸溶液,煮沸1min,冷卻至室溫后加20.00mL乙二胺四乙酸二鈉溶液,加百里酚藍(lán)溶液3~4滴,用氨水溶液中和至試液從紅色到黃色,煮沸2min。冷卻后加入10mL乙酸-乙酸鈉緩沖溶液和2滴二甲酚橙指示液,加水50mL,用氯化鋅標(biāo)準(zhǔn)滴定溶液滴定至溶液由淡黃色變?yōu)槲⒓t色即為終點(diǎn),同時(shí)做空白試驗(yàn)。
5.1.1.4 結(jié)果計(jì)算
氧化鋁(Al2O3)含量以質(zhì)量分?jǐn)?shù) 計(jì),數(shù)值以%表示,按式(2)計(jì)算:
………………………………(2)
式中:
V0——空白試驗(yàn)消耗氯化鋅標(biāo)準(zhǔn)滴定溶液的體積的數(shù)值,單位為毫升(mL);
V——試樣消耗氯化鋅標(biāo)準(zhǔn)滴定溶液的體積的數(shù)值,單位為毫升(mL);
c——氯化鋅標(biāo)準(zhǔn)滴定溶液的實(shí)際濃度的準(zhǔn)確數(shù)值,單位為摩爾每升(mol/L);
m——試料的質(zhì)量的數(shù)值,單位為克(g);
M——氧化鋁的摩爾質(zhì)量的數(shù)值,單位為克每摩爾(g/mol)(M=101.96)。
5.1.1.5 允許差
取平行測(cè)定結(jié)果的算術(shù)平均值為測(cè)定結(jié)果,平行測(cè)定結(jié)果的絕對(duì)差值:液體產(chǎn)品不大于0.1%;固體產(chǎn)品不大0.2%。
5.1.2 硫酸銅標(biāo)準(zhǔn)溶液滴定法
5.1.2.1 方法提要
在pH4.3時(shí)使EDTA與鋁離子絡(luò)合,以PAN為指示劑,用硫酸銅標(biāo)準(zhǔn)滴定溶液回滴過(guò)量EDTA溶液。
5.1.2.2 試劑和材料
5.1.2.2.1 鹽酸溶液:1+1。
5.1.2.2.2 氨水溶液:1+1。
5.1.2.2.3 緩沖溶液(pH約4.3):將42.3g無(wú)水乙酸鈉溶于水中,加80mL冰乙酸,用水稀釋至1L,搖勻。
5.1.2.2.4 乙二胺四乙酸二鈉(EDTA)溶液:c(EDTA)約0.05mol/L。
5.1.2.2.5 氧化鋁標(biāo)準(zhǔn)溶液:1mL含0.001gAl2O3。
同5.1.1.2.5。
5.1.2.2.6 1-(2-吡啶偶氮)-2-萘酚(PAN)指示溶液:將0.3gPAN溶于100mL 95%乙醇中。
5.1.2.2.7 硫酸銅標(biāo)準(zhǔn)滴定溶液:c(CuSO4)約0.025mol/L。
5.1.2.2.7.1 配制
稱(chēng)取6.3g硫酸銅(CuSO4·5H2O)溶于水,加2滴硫酸溶液(1+1),用水稀釋至1L,搖勻。
5.1.2.2.7.2 標(biāo)定
移取20.00mL EDTA溶液,置于250mL錐形瓶中,以下按5.1.2.3步驟進(jìn)行操作,讀出硫酸銅標(biāo)準(zhǔn)滴定溶液的消耗量V0,mL。
移取20.00mL EDTA溶液和20mL氧化鋁標(biāo)準(zhǔn)溶液,置于250mL錐形瓶中,以下按5.1.2.3步
驟進(jìn)行操作,讀出硫酸銅標(biāo)準(zhǔn)滴定溶液的消耗量V,mL。
5.1.2.2.7.3 結(jié)果計(jì)算
硫酸銅標(biāo)準(zhǔn)滴定溶液濃度c(CuSO4),數(shù)值以摩爾每升(mol/L)表示,按式(3)計(jì)算:
c(CuSO4)= ………………………………(3)
式中:
V1——氧化鋁標(biāo)準(zhǔn)溶液的體積的數(shù)值,單位為毫升(mL);
c1——氧化鋁標(biāo)準(zhǔn)溶液的濃度的數(shù)值,單位為克每毫升(g/mL);
M——氧化鋁的摩爾質(zhì)量的數(shù)值,單位為克每摩爾(g/mol)(M=101.96);
V0——空白消耗硫酸銅標(biāo)準(zhǔn)滴定溶液的體積的數(shù)值,單位為毫升(mL);
V——返滴定時(shí)消耗硫酸銅標(biāo)準(zhǔn)滴定溶液的體積的數(shù)值,單位為毫升(mL)。
5.1.2.3 分析步驟
用移液管移取10mL試液A,置于250mL稚形瓶中,加鹽酸溶液(1+1)2mL,煮沸1min,加20.00mL EDTA溶液,加水至約100mL,加熱至約70℃~80℃,用氨水溶液(1+1)調(diào)節(jié)pH值至3.5~4.0(用0.5~5精密pH試紙檢查),加15.00mL pH4.3緩沖溶液,煮沸2min,加4~5滴PAN指示劑,稍冷(約95℃)以硫酸銅標(biāo)準(zhǔn)滴定溶液滴定至藍(lán)紫色。同時(shí)做空白試驗(yàn)。
5.1.2.4 結(jié)果計(jì)算
氧化鋁(Al2O3)含量以質(zhì)量分?jǐn)?shù)w2,數(shù)值以%表示,按式(4)計(jì)算:
……………………………………(4)
式中:
V0——空白消耗硫酸銅標(biāo)準(zhǔn)滴定溶液的體積的數(shù)值,單位為毫升(mL);
V——試樣消耗硫酸銅標(biāo)準(zhǔn)滴定溶液的體積的數(shù)值,單位為毫升(mL);
c——硫酸銅標(biāo)準(zhǔn)滴定溶液濃度的準(zhǔn)確數(shù)值,單位為摩爾每升(mol/L);
m——試料的質(zhì)量的數(shù)值,單位為克(g);
M——氧化鋁的摩爾質(zhì)量的數(shù)值,單位為克每摩爾(g/moL),(M=101.96)。
5.1.2.5 允許差
取平行測(cè)定結(jié)果的算術(shù)平均值為測(cè)定結(jié)果,平行測(cè)定結(jié)果的絕對(duì)差值:液體產(chǎn)品不大于0.1%;固體產(chǎn)品不大于0.2%。
5.2 鹽基度的測(cè)定
5.2.1 方法提要
在試樣中加入定量鹽酸溶液,以氟化鉀掩蔽鋁離子,以氫氧化鈉標(biāo)準(zhǔn)滴定溶液滴定。
5.2.2 試劑和材料
5.2.2.1 鹽酸標(biāo)準(zhǔn)溶液:c(HCl)約0.5mol/L。
5.2.2.2 氫氧化鈉標(biāo)準(zhǔn)滴定溶液:c(NaOH)約0.5mol/L。
5.2.2.3 酚酞指示液:10g/L乙醇溶液。
5.2.2.4 氟化鉀溶液:500g/L。
稱(chēng)取500g氟化鉀,以200mL不含二氧化碳的蒸餾水溶解后,稀釋至1000mL。加入2滴酚酞指示液并用氫氧化鈉溶液或鹽酸溶液調(diào)節(jié)溶液呈微紅色,濾去不溶物后貯于塑料瓶中。